Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 40.0 - 200 MPa @Strain 0.500 - 5.00 % |
5800 - 29000 psi @Strain 0.500 - 5.00 % |
Average value: 93.9 MPa Grade Count:1 |
Overview of materials for Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled". Specific grades with glass content between 25.. |
|||
Tensile Strength, Ultimate | 40.0 - 82.7 MPa | 5800 - 12000 psi | Average value: 57.6 MPa Grade Count:28 |
Overview of materials for Acetal Copolymer, Aramid Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Acetal Copolymer, Aramid Fiber Filled". Each property range of values reported is minimum and maximum va.. |
|||
Tensile Strength, Ultimate | 40.0 - 60.0 MPa | 5800 - 8700 psi | 50 mm/min; ASTM D638 |
Solvay Specialty Polymers Solef® 3108/0903 Anti-static PVDF Compound
(discontinued **) Key features of this grade: Anti-static, Formulated. Recommended processing is injection. Available as granules.General information about SOLEF® PVDF: SOLEF® PVDF is a fluorinated semi-crystall.. |
|||
Tensile Strength, Ultimate | 40.0 - 160 MPa @Temperature 60.0 - 150 °C |
5800 - 23200 psi @Temperature 140 - 302 °F |
Average value: 104 MPa Grade Count:1 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
LyondellBasell Montell 1900CM UHMW Polyethylene Key Features: ultrahigh molecular weight polyethylene resin, excellent abrasion resistance, high impact strength, low coefficient of fraction, good chemical resistance, low odor and taste transfer, .. |
|||
Tensile Strength, Ultimate | 40.0 MPa @Temperature 22.0 °C |
5800 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Menzolit Menzolit® BMC 1100 Unsaturated Polyester UP BMC 1100 is a special BMC for high strength application. The glass content is set to a level that provides sufficient mouldability with high strength and stiffness properties. The selection of the r.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ISO 527-2/5A/500 |
Lubrizol Advanced Materials Pearlthane® 11T85 Polycaprolactone Copolyester based TPU Type : Pearlthane® 11T85 is a polycaprolactone copolyester-based thermoplastic polyurethane.Main Application : Injection MouldingSpecial Features : Adequate hardness, excellent mechanical propert.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
Hannam Chemical Hanalac 795 ABS, Pipe Grade Designed for pipe and bobbin sleeves. Excellent processability and high impact strength. Manufactured to prevent static electricity. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
Techmer ES Electrafil® DB-1200/SS/7 ABS, 7% Stainless Steel Fiber Reinforced (dry blend) Superior cost-performance when compared with other electrically conductive resins is a hallmark of Electrafil stainless steel fiber reinforced ABS. Electrafil compounds can be formulated to meet UL.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM Data |
Styron Pulse® 1350 ABS + Polycarbonate PULSE® 1350 Engineering resin offers a superior total performance with a balance of heat resistance, practical toughness, high and low temperature impact strength retention and ease of processing.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ISO 527 |
Solvay Technyl® A 205F Nylon 66, EH50 Unreinforced polyamide 66, high fluidity, fast cycling grade, for injection molding.Technyl A 205F offers two main advantages: excellent filling qualities and UL 94 V2 under 0.4 mm. It is particula.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | 20 in/min, at max load; ASTM D412 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D412 |
Lubrizol Pellethane® 2363-75D Thermoplastic Polyurethane Elastomer Feature: USP Class VIAvailable in Americas, Europe, Middle East, Africa, India and AsiaData provided by LubrizolLubrizol acquired the Pellethane product line from Dow in 2009. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | 20 in/min, at max load; ASTM D412 |
A. Schulman POLYPUR™ FPU 1112 Thermoplastic Polyurethane Compound (15% Glass) Information provided by A. Schulman. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D412 |
Lubrizol Estane® ALR E72A Thermoplastic Polyurethane Type: Estane® ALR E72A is a clear aliphatic thermoplastic polyurethane (TPU).Features: Non-yellowing with good mechanical properties.Available in AmericasInformation Provided by The Lubrizol Corpor.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
Plenco 6343 Phenolic, Granular, Compression Molded PLENCO 06343 is a mica reinforced phenolic molding compound, offering for a low power factor, low electrical losses, and good electrical properties after long exposures to high humidity. UL recogniz.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | DIN 53504 |
Lubrizol ESTANE® 54640 Ether Based Thermoplastic Polyurethane (European Grade) Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability in a flexible.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | |
Colorite Polymers 1124 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D412 |
BASF Elastollan® C-95A Polyester Type Polyurethane Elastomer Processed by extrusion or injection molding. Elastollan C series of products are polyester-based thermoplastic polyurethanes that exhibit very good hydrolytic stability. They also exhibit excellen.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | |
BASF Procom® GC20S 400 Polypropylene Uses: electrical appliance housings (e.g. drills), components requiring high impact and temperature resistance, furniture frames.Data was collected by ISO methods and provided by BASF. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ATSM D638 |
Ashley Polymers Ashlene® ABS Resin E213B General purpose, black, utility grade for injection molding with medium gloss.Data provided by the manufacturer |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | |
BCC Products BC 6126 Epoxy Surface Coat/Casting BC 6126 is a gray, low toxicity, aluminum filled, epoxy surface coat. This thixotropic resin system provides excellent surface duplication along with vertical coverage to 1/16 inch thickness. This h.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
Plaskolite West Optix® CA-1000 IG Clear High Impact Acrylic Resin High impact acrylic resin, injection molding and extrusion gradeApplications: A premium impact acrylic resin particularly suited for medical and food uses. This resin is suited for Gamma irradiatio.. |
|||
Tensile Strength, Ultimate | 40.0 MPa | 5800 psi | ASTM D638 |
Eastman Tenite Propionate 350E0096914 Natural, Trsp Cellulose Acetate Propionate Plasticizer 12%. Weight loss on heating = 0.5% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p.. |
|||
Tensile Strength, Ultimate | 40.0 - 85.0 MPa @Temperature 60.0 - 90.0 °C |
5800 - 12300 psi @Temperature 140 - 194 °F |
Average value: 78.1 MPa Grade Count:12 |
Overview of materials for Polypropylene, Long Glass Fiber 50% This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Long Glass Fiber 50%". Specific grades with glass content between 45% and 54% are include.. |
|||
Tensile Strength, Ultimate | 40.0 - 175 MPa | 5800 - 25400 psi | Average value: 105 MPa Grade Count:16 |
Overview of materials for Polybutylene Terephthalate (PBT), Carbon Black Filled This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Carbon Black Filled". Each property range of values reported is minimu.. |