SABIC Innovative Plastics LNP LUBRICOMP EFL34HL PEI (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP LUBRICOMP EFL34HL PEI (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP LUBRICOMP* EFL34HL is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ASTM D792 |
| 1.54 g/cc | 0.0556 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.170 % | 0.170 % | 50% RH, 24 hrs; ASTM D570 |
| 0.230 % | 0.230 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Time 86400 sec |
0.0030 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0033 cm/cm @Time 86400 sec |
0.0033 in/in @Time 24.0 hour |
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| 0.0060 cm/cm @Time 86400 sec |
0.0060 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 113 MPa | 16400 psi | ASTM D638 |
| 113 MPa | 16400 psi | ISO 527 | |
| Elongation at Break | 2.2 % | 2.2 % | ASTM D638 |
| 2.2 % | 2.2 % | ISO 527 | |
| Tensile Modulus | 7.40 GPa | 1070 ksi | 1 mm/min; ISO 527 |
| 7.58 GPa | 1100 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 179 MPa | 26000 psi | ASTM D790 |
| 181 MPa | 26300 psi | ISO 178 | |
| Flexural Modulus | 7.51 GPa | 1090 ksi | ASTM D790 |
| 7.94 GPa | 1150 ksi | ISO 178 | |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² | 9.52 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 32.0 kJ/m² | 15.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 8.00 J | 5.90 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 204 °C | 399 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Premix Premi-Glas® 1200H-10 Fiberglass Reinforced Thermoset SMC
- ExxonMobil Escorene® LD-767 High EVA Film and Compounding Resin (discontinued **)
- LyondellBasell Lupolen® 3025 K LDPE, Film Grade
- Saint-Gobain CHR® SG23-06(R) Primary Glass-PTFE Backing Acrylic Adhesive Pressure Sensitive Tape
- Sapco S.SiC Silicon Carbide
- A. Schulman POLYFORT™ FPP 1200H High Flow, Calcium Carbonate Fortified Homopolymer Polypropylene
- Dow Corning HS III BASE & 10:1 CLEAR CATALYST
- CP-Polymer-Technik Wellamid® 6600 PA-66-HWV0CP UL-Licensed Nylon 66, Flame Protection, Heat Stabilized, Conditioned
- EMS-Grivory Grivory® L 25 Z PA12-I
- 3M 950EK Adhesive Transfer Tapes with Adhesive 300
Copyright © lookpolymers.com All Rights Reserved