Sax Polymers SAXAMID 126F4 Nylon 6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 126F4 Nylon 6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 126F4 is a polyamide 6 injection-molding-grade reinforced with 20% glass fibers.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 g/cc | 0.0455 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 148 MPa | 21500 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 7.10 GPa | 1030 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 243 MPa | 35200 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 5.40 GPa | 783 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 8.00 kJ/m² @Temperature 23.0 °C |
3.81 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 50.0 kJ/m² @Temperature -30.0 °C |
23.8 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 53.0 kJ/m² @Temperature 23.0 °C |
25.2 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.90 J/cm² @Temperature -30.0 °C |
23.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.40 J/cm² @Temperature 23.0 °C |
25.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.700 J/cm² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.900 J/cm² @Temperature 23.0 °C |
4.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 207 °C | 405 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 214 °C | 417 °F | B/120; ISO 306 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- SABIC PP 521P Polypropylene Homopolymer for Bi-axially Oriented Film
- Palm Labs Adhesives Turbo Fuse Series 115 (20 Viscosity) Rapid Bonding Adhesive
- Polykemi AB POLYshine PBT D221 Q25 PBT, Mineral Reinforced
- DuPont Performance Polymers Delrin® FG400XRD NC010 Acetal (Unverified Data**)
- Shandong Rike Chemical HELIâ„¢ HL-35 Weather-resistance Acrylic Impact Modifier (AIM)
- Sawbones Solid Rigid Polyurethane Foam 50 pcf Density
- ChevronTexaco Gear Compounds EP J, ISO 460
- Aclo Accutech Polypropylene Copolymer CP0437W10L Wollastonite Reinforced
- Arkema Group Pebax® MV 1074 SN 01 Polyether Block Amide (PEBA) (Conditioned)
- SABIC Innovative Plastics LNP STAT-KON MD000ISC PP
Copyright © lookpolymers.com All Rights Reserved