Multibase Multi-Pro® 3014 CUW Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Multi-Pro® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Multi-Pro® 3014 CUW Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Calcium Carbonate Filler, 30% by weight.Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 14 g/10 min | 14 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Yield | 22.1 MPa | 3200 psi | ASTM D638 |
| Elongation at Break | 130 % | 130 % | ASTM D638 |
| Flexural Yield Strength | 38.6 MPa | 5600 psi | ASTM D790 |
| Flexural Modulus | 1.90 GPa | 275 ksi | ASTM D790 |
| Izod Impact, Notched | 0.694 J/cm | 1.30 ft-lb/in | 73°F; ASTM D256 |
| Gardner Impact | 12.99 J | 9.583 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 104 °C | 220 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 188 - 216 °C | 370 - 420 °F | |
| Middle Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Front Barrel Temperature | 199 - 232 °C | 390 - 450 °F | |
| Nozzle Temperature | 193 - 227 °C | 380 - 440 °F | |
| Mold Temperature | 4.44 - 65.6 °C | 40.0 - 150 °F | |
| Drying Temperature | 93.3 °C | 200 °F | |
| Dry Time | 2 hour | 2 hour | |
| Back Pressure | 0.138 - 0.345 MPa | 20.0 - 50.0 psi | |
| Screw Speed | 40 - 100 rpm | 40 - 100 rpm |
Users viewing this material also viewed the following:
- BASF Capron® 8200 NL Nylon 6 (Conditioned) (discontinued **)
- Polyram Metal Cap PB360B60 Nylon 6, 60% Mineral Filled, Heavy Density
- Zell-Metall Engineering Plastics Zellamid 1115
- A. Schulman POLYBATCH™ CE-505-E Concentrate Based In Polyethylene
- Toyobo PELPRENE™ P95C Polyester TPE, High Flexibility, High Melting Point
- Eagle Brass 200/201 Nickel Alloy, 1/8 Hardened
- ExxonMobil LDPE LD 655 Low Density Polyethylene Resin (European Grade)
- DuPont Teijin Films Melinex® 329W Polyester Film, 300 Gauge
- BASF Capron® 1202CQ Nylon 6 (Conditioned) (discontinued **)
Copyright © lookpolymers.com All Rights Reserved