BASF Ultramid® B3S HP PA6 (Dry)

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced
Manufacturer BASF
Trade Name Ultramid®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF BASF Ultramid® B3S HP PA6 (Dry).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Ultramid B3S HP is a easy flowing, finely crystalline, injection molding PA6 for fast processing
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
ISO 1183
Water Absorption 9.0 - 10 %
9.0 - 10 %
ISO 62
Moisture Absorption at Equilibrium 2.6 - 3.4 %
2.6 - 3.4 %
23°C/50% R.H.; ISO 62
Viscosity Test 145 cm³/g
145 cm³/g
Viscosity number; ISO 307
Linear Mold Shrinkage 0.0050 cm/cm
0.0050 in/in
Melt Flow 198 g/10 min

@Load 5.00 kg,
Temperature 275 °C
 198 g/10 min

@Load 11.0 lb,
Temperature 527 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength 10.0 MPa

@Strain 1.00 %,
Temperature 100 °C
 1450 psi

@Strain 1.00 %,
Temperature 212 °F
 ISO 527
18.0 MPa

@Strain 3.00 %,
Temperature 100 °C
 2610 psi

@Strain 3.00 %,
Temperature 212 °F
 ISO 527
20.0 MPa

@Strain 1.00 %,
Temperature 60.0 °C
 2900 psi

@Strain 1.00 %,
Temperature 140 °F
 ISO 527
30.0 MPa

@Strain 1.00 %,
Temperature 23.0 °C
 4350 psi

@Strain 1.00 %,
Temperature 73.4 °F
 ISO 527
40.0 MPa

@Strain 3.00 %,
Temperature 60.0 °C
 5800 psi

@Strain 3.00 %,
Temperature 140 °F
 ISO 527
40.0 MPa

@Strain 1.00 %,
Temperature -20.0 °C
 5800 psi

@Strain 1.00 %,
Temperature -4.00 °F
 ISO 527
80.0 MPa

@Strain 3.00 %,
Temperature 23.0 °C
 11600 psi

@Strain 3.00 %,
Temperature 73.4 °F
 ISO 527
100 MPa

@Strain 3.00 %,
Temperature -20.0 °C
 14500 psi

@Strain 3.00 %,
Temperature -4.00 °F
 ISO 527
Tensile Strength, Yield 90.0 MPa
13100 psi
50mm/min; ISO 527
Elongation at Yield 4.0 %
4.0 %
50mm/min; ISO 527
Modulus of Elasticity 3.40 GPa
493 ksi
ISO 527
Flexural Modulus 3.00 GPa
435 ksi
ISO 178
Izod Impact, Notched (ISO) 5.00 kJ/m²
2.38 ft-lb/in²
ISO 180/A
5.00 kJ/m²

@Temperature -30.0 °C
 2.38 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/A
Charpy Impact Unnotched 25.0 J/cm²
119 ft-lb/in²
ISO 179/1eU
20.0 J/cm²

@Temperature -30.0 °C
 95.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.400 J/cm²
1.90 ft-lb/in²
ISO 179/1eA
0.300 J/cm²

@Temperature -30.0 °C
 1.43 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 70.0 - 100 µm/m-°C

@Temperature 23.0 - 80.0 °C
 38.9 - 55.6 µin/in-°F

@Temperature 73.4 - 176 °F
 ISO 11359-1/-2
Specific Heat Capacity 1.70 J/g-°C
0.406 BTU/lb-°F
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
DIN 52612
Melting Point 220 °C
428 °F
DIN 53752
Maximum Service Temperature, Air 87.0 °C
189 °F
for 50% loss of tensile strength after 20,000 hr
97.0 °C
207 °F
for 50% loss of tensile strength after 5,000 hr
180 °C
356 °F
ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 180 °C
356 °F
ISO 75
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75
Flammability, UL94 V-2

@Thickness >=38.1 mm
 V-2

@Thickness >=1.50 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+13 ohm-cm
1.00e+13 ohm-cm
IEC 60093
Dielectric Constant 3.3

@Frequency 1.00e+6 Hz
 3.3

@Frequency 1.00e+6 Hz
 IEC 60250
Dissipation Factor 0.030

@Frequency 1.00e+6 Hz
 0.030

@Frequency 1.00e+6 Hz
 IEC 60250
Comparative Tracking Index 600 V
600 V
Test Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
Injection-molding/Extrusion
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Injection-molding
Descriptive Properties Value Comments
Color Natural
Commercial Status North America and Europe
Impact Modified No
Primary Processing Technique Injection Molding