CoorsTek AD-85 Alumina (nom. 85% Al2O3)
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CoorsTek |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CoorsTek AD-85 Alumina (nom. 85% Al2O3).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Thermal Shock Delta Tc = 300°C - Thermal shock tests are performed by quenching samples in water from different elevated temperatures. Delta Tc is the change in temperature which results in a sharp decrease in the flexural strength of the sample.Corrosion: Although all Coors Ceramics are highly resistant to chemical attack, Coors recommends obtaining specific application data from Coors before design finalization.Data Provided by the manufacturer, Coors Ceramics Co.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.42 g/cc | 0.124 lb/in³ | ASTM C20 |
| Water Absorption | 0.00 % | 0.00 % | ASTM C373 |
| Particle Size | 6.0 µm | 6.0 µm | Average Crystal Size - Thin Section Test |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Knoop Microhardness | 9.4 | 9.4 | 1000 g load |
| Hardness, Rockwell 45 N | 73 | 73 | GPa |
| Tensile Strength, Ultimate | 155 MPa | 22500 psi | ACMA Test #4 |
| Modulus of Elasticity | 221 GPa | 32100 ksi | ASTM C848 |
| Flexural Strength | 296 MPa | 42900 psi | ASTM F417 |
| Compressive Strength | 1930 MPa | 280000 psi | ASTM C773 |
| Poissons Ratio | 0.22 | 0.22 | ASTM C848 |
| Fracture Toughness | 3.00 - 4.00 MPa-m½ | 2.73 - 3.64 ksi-in½ | Notched Beam |
| Shear Modulus | 91.0 GPa | 13200 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.20 µm/m-°C @Temperature 25.0 - 1000 °C |
4.00 µin/in-°F @Temperature 77.0 - 1830 °F |
ASTM C372 |
| Specific Heat Capacity | 0.920 J/g-°C | 0.220 BTU/lb-°F | ASTM E1269 |
| Thermal Conductivity | 16.0 W/m-K | 111 BTU-in/hr-ft²-°F | ASTM C408 |
| Maximum Service Temperature, Air | 1400 °C | 2550 °F | No Load |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D1829 |
| 4.00e+8 ohm-cm @Temperature 500 °C |
4.00e+8 ohm-cm @Temperature 932 °F |
ASTM D1829 | |
| Dielectric Constant | 8.2 @Frequency 1e+6 Hz |
8.2 @Frequency 1e+6 Hz |
|
| Dielectric Strength | 9.40 kV/mm | 239 kV/in | ac; ASTM D116 |
| Dielectric Loss Index | 0.00090 | 0.00090 | at 25°C, 1 MHz; ASTM D2520 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | White |
Users viewing this material also viewed the following:
- Polyplastic Torlen® PE 2K 901 High Density Polyethylene, Carbon Filled
- NanoAmor 95%, OD/ID: < 8/2-5 nm Aligned Multi-Walled Carbon Nanotubes
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 3.0 PHR MBT
- SK Chemicals SKYTHANE® 190A S series Polyurethane
- Colorite Polymers CS6038SR Wire and Cable Insulation Vinyl Compound
- ExxonMobil Bicor® 310 AB OPP Film
- AK Steel 17-7 PH® Precipitation Hardening Stainless Steel, Condition A
- Compuestos Dominicanos Polycom VN-051090 PVC Compound
- Solvay Specialty Polymers Algoflon® L100 Polytetrafluoroethylene (PTFE) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved