- Lanxess Durethan® BKV 30 N1 000000 Nylon 6, 30% Glass Fiber
Lanxess Durethan® BKV 30 N1 000000 Nylon 6, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 30 N1 000000 Nylon 6, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6, 30% glass fiber, injection molding, flame retardantInformation provided by LANXESS.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 5.1 % | 5.1 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0022 cm/cm | 0.0022 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | 60x60x2; 280°C / MT 80°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 80.0 MPa | 11600 psi | at yield, conditioned, 50 mm/min; ISO 527-1,-2 |
| 80.0 MPa | 11600 psi | conditioned, 5 mm/min; ISO 527-1,-2 | |
| 140 MPa | 20300 psi | 5 mm/min; ISO 527-1,-2 | |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527-1,-2 |
| 3.6 % | 3.6 % | conditioned, 5 mm/min; ISO 527-1,-2 | |
| Elongation at Yield | 3.5 % | 3.5 % | conditioned, 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 6.50 GPa | 943 ksi | conditioned, 1 mm/min; ISO 527-1,-2 |
| 11.7 GPa | 1700 ksi | 1 mm/min; ISO 527-1,-2 | |
| Flexural Strength | 145 MPa | 21000 psi | conditioned, 2 mm/min; ISO 178-A |
| 230 MPa | 33400 psi | 2 mm/min; ISO 178-A | |
| Flexural Modulus | 7.50 GPa | 1090 ksi | conditioned, 2 mm/min; ISO 178-A |
| 11.0 GPa | 1600 ksi | 2 mm/min; ISO 178-A | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | conditioned; ISO 180-1U |
| 50.0 kJ/m² | 23.8 ft-lb/in² | ISO 180-1U | |
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C |
21.4 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 179-1eU |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eU | |
| 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 6.00 J/cm² @Temperature -30.0 °C |
28.6 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
conditioned; ISO 179-1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
conditioned; ISO 179-1eA | |
| Puncture Energy | 5.00 J @Temperature -30.0 °C |
3.69 ft-lb @Temperature -22.0 °F |
ISO 6603-2 |
| 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ISO 6603-2 | |
| 9.00 J @Temperature 23.0 °C |
6.64 ft-lb @Temperature 73.4 °F |
conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
11.1 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature 23.0 - 55.0 °C |
50.0 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1,-2 |
| Melting Point | 225 °C | 437 °F | 10 °C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 135 °C | 275 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 200 °C | >= 392 °F | 50 N; 120 °C/h; ISO 306 |
| >= 200 °C | >= 392 °F | 50 N; 50 °C/h; ISO 306 | |
| Flammability, UL94 | V-1 @Thickness 1.60 mm |
V-1 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 32 % | 32 % | Method A; ISO 4589-2 |
| Glow Wire Test | 775 °C @Thickness 1.60 mm |
1430 °F @Thickness 0.0630 in |
GWIT; IEC 60695-2-12 |
| 775 °C @Thickness 3.00 mm |
1430 °F @Thickness 0.118 in |
GWIT; IEC 60695-2-12 | |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695-2-12 | |
| 960 °C @Thickness 3.00 mm |
1760 °F @Thickness 0.118 in |
GWFI; IEC 60695-2-12 | |
| Shrinkage | 0.0400 % @Temperature 120 °C, Time 14400 sec |
0.0400 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, transverse, 60x60x2; ISO 294-4 |
| 0.120 % @Temperature 120 °C, Time 14400 sec |
0.120 % @Temperature 248 °F, Time 4.00 hour |
post-shrinkage, 60x60x2; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | conditioned; IEC 60093 |
| 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 | |
| Dielectric Constant | 4.2 @Frequency 1.00e+6 Hz |
4.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.5 @Frequency 1.00e+6 Hz |
4.5 @Frequency 1.00e+6 Hz |
conditioned; IEC 60250 | |
| 4.7 @Frequency 100 Hz |
4.7 @Frequency 100 Hz |
IEC 60250 | |
| 8.0 @Frequency 100 Hz |
8.0 @Frequency 100 Hz |
conditioned; IEC 60250 | |
| Dielectric Strength | 27.0 kV/mm | 686 kV/in | conditioned; IEC 60243-1 |
| 28.0 kV/mm | 711 kV/in | IEC 60243-1 | |
| Dissipation Factor | 0.013 @Frequency 100 Hz |
0.013 @Frequency 100 Hz |
IEC 60250 |
| 0.019 @Frequency 1.00e+6 Hz |
0.019 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 0.045 @Frequency 1.00e+6 Hz |
0.045 @Frequency 1.00e+6 Hz |
conditioned; IEC 60250 | |
| 0.13 @Frequency 100 Hz |
0.13 @Frequency 100 Hz |
conditioned; IEC 60250 | |
| Comparative Tracking Index | 350 V | 350 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Injection molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection molding; ISO 294 |
| Dry Time | 2.00 - 6.00 hour @Temperature 80.0 °C |
2.00 - 6.00 hour @Temperature 176 °F |
Users viewing this material also viewed the following:
- Nilit Nilamid B3N Unfilled, Nucleated PA6
- Quadrant EPP Ketron® CA30 LSG PEEK, Extruded 30% Carbon Fiber Reinforced Polyetherether Ketone (ASTM Product Data Sheet)
- Northstar Polymers SBX-146 Curing Agent
- Momentive Performance Materials Siloprenâ„¢ FSL 7661 Fluorinated Liquid Silicone Rubber
- Dow Corning SILASTIC® 94-595-HC SILICONE RUBBER PART A&B
- Ascend Performance Materials Vydyne® 20NSP1 Nylon 66, Conditioned
- Haynes 625 alloy, 30% cold reduction, 1010°C anneal for 5 minutes
- Bostik 6305 Good Heat Resistance EVA Glue Stick
- ChevronTexaco Ulti-Plex® HV Synthetic Grease EP
Copyright © lookpolymers.com All Rights Reserved