Polymer Property : Flexural Modulus = 1600 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	11.0 GPa	1600 ksi
Plastcom SLOVASTER® E GF 30 PBT, 30% glass fibre FeaturesPET for injection moulding, chemically reinforced with 30% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bending..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Nylene® PA6/6 Glass Filled 5143 HS Nylon 6/6 43% Glass Filler; Property data for dry as molded samples.ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeric Resources Corporation.
Flexural Modulus	11.0 GPa	1600 ksi	1.3 mm/min; ASTM D790
Ovation Polymers Opnyl OP6GF43 Nylon 6, 43% Glass Reinforced, Dry Nylon 6 - Glass reinforced (43 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
Flexural Modulus	11.0 GPa	1600 ksi	Tangent; ASTM D790
Premix Premi-Glas® 1261-28 VE Glass Reinforced Vinyl Ester TMC Description: Premi-Glas® 1261-28 VE is a glass reinforced vinyl ester molding compound designed for automotive under the hood applications. Key features and benefits: Excellent thermal stability an..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1301-8456 PPS, linear, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.High-strength and stiff parts w..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1700-7859 PPO, with carbon fiber, glass fiber and PTFE Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts; low thermal coefficient of expansion.Improved friction and wear behaviour...
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1850-7783-1 PBT, with glass fiber, PTFE, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Improved friction and wear behaviour. Emergency running property.High dimensionally stable prec..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 21-8113 Polyamide 6/6T, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Flexural Modulus	11.0 - 11.7 GPa	1600 - 1700 ksi	ASTM D790
Mar-Bal MB2000-25 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can..
Flexural Modulus	11.0 GPa	1600 ksi	2 mm/min; ISO 178-A
Lanxess DurethanÂ® BKV 140 DUS008 000000 Nylon 6, 40% Glass Fiber PA 6, 40% glass fibers, injection molding, impact modifiedInformation provided by LANXESS.
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1301-7869/BL PPS, linear, with glass fiber Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High-strength and stiff parts with low creep.High continuous use and heat distortion temperature. ..
Flexural Modulus	11.0 GPa @Temperature 22.0 Â°C	1600 ksi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® BMC 3100 Unsaturated Polyester UP BMC 3100 is a special BMC suitable for the use in head lamp reflectors. Because of its high temperature resistance and dimensional stability as well as low coefficient of thermal expansion, complex ..
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Solvay TECHNYLÂ® A 218 V43 Black 21 N PA66, 43% glass fiber, DRY Description: Polyamide PA66, reinforced with 43% of glass fiber, heat stabilized, for injection molding.Available in: North AmericaProduct Applications: TECHNYLÂ® A 218 V43 is used in all sectors ..
Flexural Modulus	11.03 GPa	1600 ksi	ASTM D790
SABIC Innovative Plastics LNP LUBRICOMP OFL36A PPS - Branched LNP* LUBRICOMP* OFL36A is a compound based on PPS - Branched resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Wear Resistant.
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Solvay Specialty Polymers AmodelÂ® A-6135 HN Polyphthalamide (PPA), 35% Glass Fiber (Conditioned) AmodelÂ® A-6135 HN polyphthalamide (PPA) is a 35% glass reinforced resin that is heat stabilized, lubricated and hot-water moldable. Key properties of the resin are high heat resistance, high stre..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Techmer ES HiFillÂ® PA4/6 GF40 HS 40% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber Reinforcement, 40% Filler by WeightAdditive: Heat StabilizerFeatures: Heat StabilizedTPCI# 9627150Information provided by T..
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Chevron Phillips Xtel® XE4050BL Polyphenylene Sulfide Alloy Xtel® XE4050BL is a glass fiber and mineral filled PPS based alloy developed to provide high ductility and impact strength along with good thermal stability.Information provided by Chevron Phillips..
Flexural Modulus	11.0 GPa	1600 ksi	cond; ISO 178
DSM Stanyl® TS250F8 PA46-GF40 FR 40% Glass Reinforced, Flame Retardant, Heat Stabilized
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
A. Schulman ComAlloy Lubrilon® 632 Nylon 6/6, Carbon Fiber/PTFE Filled Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Resinoid 2002-2 Phenolic Molding, Fabric Reinforced Data provided by the manufacturer.The Resinoid 2000 organic fiber reinforced series compounds feature mechanical strength, dimensional stability, and shock resistance
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOM® 1-7003 Polyamide 66, with carbon fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Electrically conductive, suita..