Polymer Property : Flexural Modulus = 11.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	11.0 GPa	1600 ksi	1.3 mm/min; ASTM D790
Ovation Polymers Opnyl OP6GF43 Nylon 6, 43% Glass Reinforced, Dry Nylon 6 - Glass reinforced (43 %), high tensile strength, stiffness and HDT. *All properties are measured after 48 hours of conditioning at 23°C and 50% relative humidity. For Nylon compounds the m..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Niche Polymer PA66GF43BK Nylon 66, 43% Glass Fiber Filled Information provided by Niche Polymer
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Niche Polymer PA6GF43BK Nylon 6, 43% Glass Fiber Filled Information provided by Niche Polymer
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Global GP-5180-30 PET 30% Glass Reinforced PET Polyester (discontinued **) Information provided by Global Polymers Corporation.
Flexural Modulus	11.0 GPa	1590 ksi	ASTM D790
Polymer Resources NY66-G43-[color]H Nylon, 43% Glass Reinforced, Heat Stabilized (DAM) Process: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples. Nylon grades are tested dry as molded (DAM).Information provide..
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Victrex® PEEK 450GL30 Polyetheretherketone, 30% Glass Fiber, Black Product Description: High performance thermoplastic material, 30% glass fiber reinforced PolyEtherEtherKetone (PEEK), semi crystalline, granules for injection moulding and extrusion, Standard viscos..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 21-7928 Polyamide 6/6T, with carbon fiber, lubricant modified Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.Strong, stiff parts.Dynamic stressed parts at high movement velocity.Improved friction and wear..
Flexural Modulus	11.0 GPa @Temperature 22.0 Â°C	1600 ksi @Temperature 71.6 Â°F	25 mm wide 100 mm long, flat samples; ISO 14125
Menzolit MenzolitÂ® BMC 0410 Unsaturated Polyester UP BMC 0410 is a low profile BMC with zero shrinkage and low coefficient of thermal expansion. It is especially suited for precision mouldings in office and communication equipment. The combination of ..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1/CF/20/TF/5 Polyamide 66, with carbon fiber and PTFE, heat stabilized Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Improved friction and wear beh..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1105-7373 PEEK, with carbon fiber, lubricant modified Applications: Automotive industry, textile machinery, medical- and precision engineering, aircraft industry.Strong, stiff parts; low thermal coefficient of expansion.Chemical and hydrolysis resistan..
Flexural Modulus	11.0 GPa	1600 ksi
Lehmann & Voss LUVOCOMÂ® 1301-7767 PPS, linear, with carbon fiber, lubricant modified Applications: Automotive industry, textile-and office machinery, medical- and precision engineering.High continuous use and heat distortion temperature. Non flammable.Strong, stiff parts.Suitable fo..
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Solvay Specialty Polymers AmodelÂ® DW-1130 Polyphthalamide (PPA), 30% Glass Fiber AmodelÂ® DW-1130 is a 30% glass-fiber-reinforced resin designed for high strength and stiffness and improved hydrolytic stability. This material has low moisture absorption and a low coefficient o..
Flexural Modulus	11.0 GPa	1600 ksi	ISO 178
Solvay Specialty Polymers AmodelÂ® HFZ A-4133L Polyphthalamide (PPA), 33% Glass Fiber AmodelÂ® HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a b..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Sumitomo Bakelite North America RXÂ® 431 Cellulose Reinforced Phenolic Novolac RX431 is a cellulose fiber reinforced phenolic novolac molding compound. This material is recommended for large parts requiring moderate toughness. It is designed to meet the requirements of ASTM D..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Techmer ES ElectrablendÂ® PA6/6 03003 CF Carbon Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Carbon Fiber ReinforcementAdditive: Lubricant, Impact Modifier and Heat StabilizerFeatures: Lubricated, Electrically Conductive, Impact..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
Ensinger Tecatron® XP-86 Compression Molded PPS Compound, with 40% Carbon Fiber Ensinger Special Polymers has over twenty different grades of TECATRON PPS available. Custom formulations can be blended to suit specific applications. Compression molding is amenable to short run p..
Flexural Modulus	11.0 GPa	1600 ksi	DAM; ISO 178
DuPont Performance Polymers Zytel® 77G43L BK031 Nylon 612 (Unverified Data**) 43% Glass Reinforced Polyamide 612Information provided by DuPont Performance Polymers
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
A. Schulman ComAlloy Lubrilon® 632 Nylon 6/6, Carbon Fiber/PTFE Filled Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulma..
Flexural Modulus	11.0 GPa	1600 ksi	ASTM D790
LATI LARTON G/30 30% Glass Fiber Filled Polyphenylene sulfide (PPS) (discontinued **) Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..