Braskem Green PE SLL118/21 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene

Category Polymer , Film , Renewable/Recycled Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Braskem
Trade Name Green PE
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem Green PE SLL118/21 Blow Film Extrusion and Cast Film Extrusion Linear Low Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: SLL118/21 is a LLDPE Butene copolymer produced by Braskem. It is a general purpose product that shows a good processing performance balanced with good optical and mechanical properties as well as sealability. Very low gel amount. The minimum biobased content of this grade is 87%, determined according to ASTM D6866. Additive: Antiblocking Medium; Slip Medium Applications: Automatic Packaging (FFS); liners; general purpose; HDPE and LDPE blends.Information provided by Braskem.
Physical Properties Metric English Comments
Specific Gravity 0.919 g/cc
0.919 g/cc
ASTM D1505/D792
Thickness 38.0 microns
1.50 mil
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 1070 %
1070 %
ASTM D882
Film Elongation at Break, TD 1340 %
1340 %
ASTM D882
Elmendorf Tear Strength MD 180 g
180 g
gF; ASTM D1922
Elmendorf Tear Strength TD 400 g
400 g
gF; ASTM D1922
Dart Drop Test 130 g
0.287 lb
g/F50; ASTM D1709
Film Tensile Strength at Break, MD 40.0 MPa
5800 psi
ASTM D882
Film Tensile Strength at Break, TD 30.0 MPa
4350 psi
ASTM D882
1% Secant Modulus, MD 210 MPa
30500 psi
ASTM D882
1% Secant Modulus, TD 230 MPa
33400 psi
ASTM D882