Polymer Property : Tensile Strength at Break = 11600 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	80.0 MPa	11600 psi
Plastcom SLOVALEN PH 59 GF 30 PP, 30% glass fibre FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 30% glass fibre, with high strength, rigidity and toughness, adapted thermal properties, decreased shrinkage. Suita..
Tensile Strength at Break	80.0 MPa	11600 psi
Plastcom SLOVAMID 6 FRM1X3 PA6, flame retardant FeaturesDetermined for electrotechnical use. Delivered in natural mode. PA 6 for injection moulding with reduced flammability, with nonhalogen flame retardant. Excellent fluidity of the material pre..
Tensile Strength at Break	80.0 MPa	11600 psi
Radici Radilon® S CP400 (dry) Nylon 6 Radilon® S is a range of polyamide 6 (PA6) products obtained through the polymerization of caprolactam and used for injection, extrusion and blow-molding.Information provided by Radici group.
Tensile Strength at Break	80.0 MPa @Temperature 23.0 °C	11600 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Rynite® 415HP BK503 PET (Unverified Data**) Rynite® 415HP BK503 is a 15% glass reinforced modified polyethylene terephthalate with improved for easy, fast processing over a broad molding range with excellent balance of strength, stiffness, a..
Tensile Strength at Break	80.0 MPa	11600 psi	Molded; ASTM D882
Honeywell Aegisâ„¢ H135MP Nylon 6 Extrusion Grade Homopolymer Film Description: Aegis H135MP is a lubricated and nucleated high viscosity, nylon 6 extrusion grade homopolymer for cast or blown film. It conforms to Food and Drug Administration requirements of 21 CFR..
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527
Grupo Repol DinalonÂ® A3S25 PA66 Unreinforced Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527-1/-2
Mitsubishi XantarÂ® MX 1081 Polycarbonate-10% Glass Reinforced XantarÂ® materials are engineered for performance, consistency and reliability. This makes XantarÂ® resins ideal for interior automotive components, electrical equipment and consumer appliances ..
Tensile Strength at Break	80.0 MPa	11600 psi	d.a.m.; ISO 527-1, -2; 5 mm/min
Lanxess DurethanÂ® BKV 215 H2.0 DUS008 901510 Nylon 6, Impact Modified PA 6, 15% glass fibers, injection molding, impact modified, heat-aging stabilizedInformation provided by LANXESS.
Tensile Strength at Break	80.0 MPa	11600 psi
Lushan PP+GF30%+4% PR-3 Maleic Anhydride Grafted Polypropylene Malic anhydride grafted polypropylene (PP-a-MAH) Lushan series is evaluated as compatiblizer/coupling agent which is used to fill or reinforced polypropylene. As the coupling agent, PP-g-MAH can sig..
Tensile Strength at Break	80.0 MPa	11600 psi	10mm/min; ASTM D638
Kingfa PA6-T25 25% Mineral Filled PA6 Features:Low tendency to wrapApplications:Injection moldingSport applianceAutomobile partsPower toolsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Tensile Strength at Break	80.0 MPa	11600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Ultem DT1810E PEI Blend (Asia Pacific) Improved ductility, transparent, enhanced flow Polyetherimide blend (Tg 200C) with internal mold release and enhanced ductility. ECO Conforming.This data was supplied by SABIC-IP for the Asia Pacifi..
Tensile Strength at Break	80.0 MPa	11600 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL LTA1350 PPE+PS Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No..
Tensile Strength at Break	80.0 MPa	11600 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ValoxÂ® VX4910 ASA+PBT (Europe-Africa-Middle East) 10% Glass reinforced nucleated PBT/ASA with excellent mechanical properties high dimensional stability, and low density.
Tensile Strength at Break	80.0 MPa	11600 psi	50 mm/min; ISO 527
SABIC Innovative Plastics NORYL LTA1350 PPE+PS (Europe-Africa-Middle East) Noryl* LTA1350 is an unfilled, injection moldable grade. Designed for improved long term heat aging, this resin also uses non-chlorinated, non-brominated FR additives to achieve a V0 UL94 rating. No..
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527-93
Wellman Wellamid® 22L-BL Engineering Grade Nylon 66 Description: Engineering Grade Nylon 66Information provided by Wellman.
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527-93
Wellman Wellamid® NY1599-GY Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman.
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527-93
Wellman Wellamid® NY1615-BK Unfilled Nylon 66 Description: Unfilled Nylon 66Information provided by Wellman.
Tensile Strength at Break	80.0 MPa	11600 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6000 MR 309 HWCP Mineral Nylon 6, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527
Eurotec® Tecomid® NB40 MR30 NL PA 6 30% mineral reinforced Excellent stiffness/toughness balanceHigh mechanical strengthVery good thermal stabilityExcellent flammability characteristicsGood electrical propertiesHigh wear resistance and low frictionVery good..
Tensile Strength at Break	80.0 MPa	11600 psi	50%RH; ISO 527-1/-2
DuPont Performance Polymers Minlon® 73GM40 NC010 Nylon 6 (Unverified Data**) 40% Mineral/Glass Reinforced Polyamide 6 Minlon 73GM40 NC010 is a 40% mineral/glass reinforced heat stabilized polyamide 6 resin for injection molding.Information provided by DuPont Performance Poly..
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527
Eurotec® Tecotek® PC44 GR10 GR003 ZG70 PC, 10% glass fiber reinforced, flame retardant - halogen (RoHS compliant), light grey Information provided by Eurotec®
Tensile Strength at Break	80.0 MPa	11600 psi	ISO 527
BASF Petra® 7010 WT 7729 15% Glass Filled PET Description: Petra 7010 WT7729 is a 15% glass fiber reinforced, pigmented white injection molding compound based on post-consumer recycle polyethylene terephthalate. Formulated for superior surface ..
Tensile Strength at Break	80.0 MPa @Temperature -40.0 °C	11600 psi @Temperature -40.0 °F	ASTM Test
BASF Ultramid® 8202 HS PA6 (Conditioned) Ultramid 8202 HS is a heat stabilized, low viscosity, general purpose nylon 6 injection molding homopolymer. It possesses the combination of strength and toughness and has excellent chemical and ab..
Tensile Strength at Break	80.0 MPa	11600 psi	TD
BASF Ultramid® C33 LN 0.025 mm Blown Film PA6/66 Description: Ultramid® C33 LN is a copolyamide 6/66 grade of intermediate viscosity for the production of mulitlayer film. Its lower melting point than standard PA 6 is advantageous for coextrusion..
Tensile Strength at Break	80.0 MPa	11600 psi	ASTM D638
Beijing Chemical Industry KAIFA® 551-GT30S PBT Resin Glass fiber and mineral filled, flame retardant, low warpage, superior electrical performanceInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break	80.0 MPa	11600 psi	ASTM D638
Beijing Chemical Industry KAIFA® HN301-G10 PA6 Resin 10% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break	80.0 MPa	11600 psi	ASTM D638
Aclo Accutech Nylon 6 NY0730G10L Glass Reinforced
Tensile Strength at Break	80.0 MPa	11600 psi	Conditioned; ISO R 527
Addiplast Addinyl B2I V25 Flame Retardant Nylon 6, 25% Glass Filled Flame retardant, 25% glass fiber reinforced, halogen freeInformation provided by Addiplast.
Tensile Strength at Break	80.0 MPa @Temperature 160 - 175 °C, Time 1.80e+7 sec	11600 psi @Temperature 320 - 347 °F, Time 5000 hour	5 [mm/min], 50% Loss of Tensile Strength; ICE 216
Akro-Plastic Akromid® A3 GF 20 (2419) PA 6.6 Dry, 20% Glass Filled AKROMID® A (Polyamide 6.6) is an engineering compound, characterized by high mechanical strength, stiffness and thermal resistance. Furthermore, this polyamide offers high toughness at low temperat..
Tensile Strength at Break	80.0 MPa	11600 psi	5 mm/min; ISO 527
SABIC Innovative Plastics Valox® VX4015 PBT (Europe-Africa-Middle East) VALOX VX4015 is a 15% glass reinforced PBT injection moulding resin, with excellent hydrolytical stability.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.