SABIC Innovative Plastics LNP LUBRICOMP JX00061 PES (Europe-Africa-Middle East)

Category	Polymer , Thermoplastic , Polyethersulfone (PES)
Manufacturer	SABIC Innovative Plastics (GE Plastics)
Trade Name	LNP LUBRICOMP
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	SABIC Innovative Plastics LNP LUBRICOMP JX00061 PES (Europe-Africa-Middle East).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LNP* Lubricomp* JX00061 is a compound based on Polyethersulfone resin containing Carbon Fiber, Proprietary Lubricant. Added features of this material include: Electrically Conductive.

Physical Properties	Metric	English	Comments
Density	1.53 g/cc	0.0553 lb/inÂ³	ISO 1183
Linear Mold Shrinkage, Flow	0.0010 - 0.0030 cm/cm	0.0010 - 0.0030 in/in	on Tensile Bar; SABIC Method

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	104 MPa	15100 psi	5 mm/min; ISO 527
Elongation at Break	1.4 %	1.4 %	5 mm/min; ISO 527
Tensile Modulus	10.0 GPa	1450 ksi	1 mm/min; ISO 527
Flexural Strength	139 MPa	20200 psi	2 mm/min; ISO 178
Flexural Modulus	7.70 GPa	1120 ksi	2 mm/min; ISO 178
Izod Impact, Notched (ISO)	6.00 kJ/mÂ²	2.86 ft-lb/inÂ²	80104; ISO 180/1A
Izod Impact, Unnotched (ISO)	20.0 kJ/mÂ²	9.52 ft-lb/inÂ²	80104; ISO 180/1U

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	16.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	8.89 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
CTE, linear, Transverse to Flow	51.0 Âµm/m-Â°C @Temperature 23.0 - 60.0 Â°C	28.3 Âµin/in-Â°F @Temperature 73.4 - 140 Â°F	ISO 11359-2
Deflection Temperature at 0.46 MPa (66 psi)	226 Â°C	439 Â°F	Flatw 80104 sp=64mm; ISO 75/Bf
Deflection Temperature at 1.8 MPa (264 psi)	221 Â°C	430 Â°F	Flatw 80104 sp=64mm; ISO 75/Af

Electrical Properties	Metric	English	Comments
Surface Resistance	10 - 10000 ohm	10 - 10000 ohm	ASTM D257

Users viewing this material also viewed the following: