Lanxess Durethan® BKV 15 H3.0 000000 Nylon 6 Copolymer, 15% Glass Fibers
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® BKV 15 H3.0 000000 Nylon 6 Copolymer, 15% Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 6 Copolymer, 15% glass fibers, injection molding, heat-ageing stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm @Thickness 2.00 mm |
0.0040 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 2.00 mm |
0.0060 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | Conditioned; ISO 527-1,-2 |
| 125 MPa | 18100 psi | ISO 527-1,-2 | |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1,-2 |
| 12 % | 12 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 3.60 GPa | 522 ksi | Conditioned; ISO 527-1,-2 |
| 6.00 GPa | 870 ksi | ISO 527-1,-2 | |
| Flexural Strength | 120 MPa @Strain 8.00 % |
17400 psi @Strain 8.00 % |
Conditioned; ISO 178 |
| 200 MPa @Strain 5.00 % |
29000 psi @Strain 5.00 % |
ISO 178 | |
| Flexural Yield Strength | 90.0 MPa @Strain 3.50 % |
13100 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 201 MPa @Strain 3.50 % |
29200 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 3.10 GPa | 450 ksi | Conditioned; ISO 178 |
| 5.60 GPa | 812 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U |
| 35.0 kJ/m² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U | |
| 35.0 kJ/m² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -40.0 °C |
<= 4.76 ft-lb/in² @Temperature -40.0 °F |
Conditioned; ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 80.0 µm/m-°C | 44.4 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 213 °C | 415 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 200 °C @Load 5.10 kg |
>= 392 °F @Load 11.2 lb |
120°C/h; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C @Diameter 2.00 mm |
1200 °F @Diameter 0.0787 in |
IEC 60695-2-12 |
| Shrinkage | 0.10 % @Temperature 120 °C, Time 14400 sec |
0.10 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.10 % @Temperature 120 °C, Time 14400 sec |
0.10 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | Conditioned; IEC 60093 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | Conditioned; IEC 60093 |
| 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | |
| Dielectric Constant | 3.7 @Frequency 1.00e+6 Hz |
3.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.6 @Frequency 100 Hz |
4.6 @Frequency 100 Hz |
IEC 60250 | |
| 4.6 @Frequency 1.00e+6 Hz |
4.6 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 19 @Frequency 100 Hz |
19 @Frequency 100 Hz |
Conditioned; IEC 60250 | |
| Dielectric Strength | 22.0 kV/mm @Thickness 1.00 mm |
559 kV/in @Thickness 0.0394 in |
Conditioned; IEC 60243-1 |
| 35.0 kV/mm @Thickness 1.00 mm |
889 kV/in @Thickness 0.0394 in |
IEC 60243-1 | |
| Dissipation Factor | 0.030 @Frequency 100 Hz |
0.030 @Frequency 100 Hz |
IEC 60250 |
| 0.038 @Frequency 100 Hz |
0.038 @Frequency 100 Hz |
IEC 60250 | |
| 0.12 @Frequency 1.00e+6 Hz |
0.12 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| 0.38 @Frequency 1.00e+6 Hz |
0.38 @Frequency 1.00e+6 Hz |
Conditioned; IEC 60250 | |
| Comparative Tracking Index | 500 V | 500 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | Recommended |
| 280 °C | 536 °F | Processing conditions for test specimens; ISO 294 | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 100 °C | 176 - 212 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | Passed US-FMVSS302 | ISO 3795 |
| ISO Shortname | ISO 1874-PA 6/66,GHR,14-060,GF15 |
Users viewing this material also viewed the following:
- MV Labs CD1000 CdSO4·xH2O Cadmium sulfate hydrate
- RheTech Products FT7011-01 Thermoplastic Polyolefin, Non-UV Stabilized, Black
- Ravago Manufacturing Americas Enviramid™ N1300HL Nylon 66
- Lehmann & Voss LUVOTECH® MR 1025 BK Polyamide 66, with mineral filler
- Indium Corp. Indalloy 24 Bismuth Solder Alloy
- Multibase Multibatch® MP 53658 Sheet Extrusion
- Master Bond EP51FL-1 Rapid Curing Cryogenic Two Component Epoxy
- A. Schulman POLYBATCH™ White 8350/UV5 Concentrate Based In Polyethylene
- Toyobo Vylopet® EMC145 Glass Reinforced Polyester, Standard Grade
Copyright © lookpolymers.com All Rights Reserved