Lanxess Durethan® B 30 S FN30 000000 Nylon 6, Flame Retardant

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced, Flame Retardant
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® B 30 S FN30 000000 Nylon 6, Flame Retardant.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 6, non-reinforced, injection molding, halogen free flame retardant, heat-aging resistanceInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ISO 1183
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0090 cm/cm
0.0090 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0030 cm/cm
0.0030 in/in
Post-shrinkage, 60x60x2; 120°C; 4 hour; ISO 294-4
0.0090 cm/cm
0.0090 in/in
60x60x2; 260°C / MT 80°C; 600 bar; ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Yield 80.0 MPa
11600 psi
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Break 9.0 %
9.0 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Elongation at Yield 3.8 %
3.8 %
d.a.m.; ISO 527-1, -2; 50 mm/min
Tensile Modulus 3.50 GPa
508 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 120 MPa

@Strain 5.50 %
 17400 psi

@Strain 5.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 105 MPa

@Strain 3.50 %
 15200 psi

@Strain 3.50 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Modulus 3.30 GPa
479 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Unnotched (ISO) 100 kJ/m²
47.6 ft-lb/in²
d.a.m.; ISO 180-1U
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 1.8 MPa (264 psi) 65.0 °C
149 °F
ISO 75-1, -2
Flammability, UL94 V-0

@Thickness 0.380 mm
 V-0

@Thickness 0.0150 in
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
V-0

@Thickness 3.00 mm
 V-0

@Thickness 0.118 in
Oxygen Index 40 %
40 %
Method A; ISO 4589-2
Glow Wire Test 775 °C

@Diameter 0.400 mm
 1430 °F

@Diameter 0.0157 in
 GWIT; IEC 60695-2-13
775 °C

@Diameter 0.800 mm
 1430 °F

@Diameter 0.0315 in
 GWIT; IEC 60695-2-13
775 °C

@Diameter 1.50 mm
 1430 °F

@Diameter 0.0591 in
 GWIT; IEC 60695-2-13
960 °C

@Diameter 0.400 mm
 1760 °F

@Diameter 0.0157 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 0.800 mm
 1760 °F

@Diameter 0.0315 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 1.50 mm
 1760 °F

@Diameter 0.0591 in
 GWFI; IEC 60695-2-12
960 °C

@Diameter 3.00 mm
 1760 °F

@Diameter 0.118 in
 GWFI; IEC 60695-2-12
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 1.00e+16 ohm
1.00e+16 ohm
d.a.m.; IEC 60167
Dielectric Strength 31.0 kV/mm

@Thickness 1.00 mm
 787 kV/in

@Thickness 0.0394 in
 d.a.m.; IEC 60243-1
Processing Properties Metric English Comments
Melt Temperature 250 - 270 °C
482 - 518 °F
260 °C
500 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 100 °C
176 - 212 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.070 %
0.030 - 0.070 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA 6, GFHR, 12-030; ISO 1043-PA FR (30)