SABIC Innovative Plastics Cycolac® BDT6500 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® BDT6500 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
AUTOMOTIVE. Low gloss, color concentratable for interior applications. Natural only.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Viscosity | 155000 cP | 155000 cP | Melt Viscosity, 260°C, 1000 sec-1; ASTM D3825 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 3.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Spiral Flow | 86.36 cm @Temperature 260 °C |
34.00 in @Temperature 500 °F |
10 ips,3.175 X 1524 mm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 72.0 MPa | 10400 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 1.86 J/cm | 3.48 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 42.0 J | 31.0 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 155 µm/m-°C @Temperature -40.0 - 60.0 °C |
86.1 µin/in-°F @Temperature -40.0 - 140 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 93.0 °C @Thickness 3.20 mm |
199 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C @Thickness 3.20 mm |
178 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 85.0 °C @Thickness 6.40 mm |
185 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI, Electrical | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical with Impact | 60.0 °C | 140 °F | UL 746B |
| UL RTI, Mechanical without Impact | 60.0 °C | 140 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 25 % | 25 % | untextured, 60 degrees; ASTM D523 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 400 - 600 V | 400 - 600 V | UL 746A |
| Hot Wire Ignition, HWI | 7.0 - 15 sec | 7.0 - 15 sec | UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | UL 746A |
Users viewing this material also viewed the following:
- Precision Polymer Engineering S70U Silicone Rubber
- Kraton® G1730 M (SEP) Linear Diblock Copolymer
- Karina E 754-10/426-AT-IS White PVC Compound
- SABIC Innovative Plastics LNP Thermocomp EB004 PEI
- SABIC Innovative Plastics LNP STAT-KON EX08318C PEI (Asia Pacific)
- Schmolz + Bickenbach UGIMA® 303 Stainless Steel Bar
- Lubrizol ESTANE® GP85AE Ester Based Thermoplastic Polyurethane
- UBE UBESTA® 3030U Nylon 12 (After Hydrochloric Acid (10%) for 1000 hours)
- ConocoPhillips Hydroclear® El Mar® Low Ash Heavy Duty SAE 40
- 3M 7908FL Screen Printable Sheet Polyester Label Material
Copyright © lookpolymers.com All Rights Reserved