Lanxess Durethan® AKV 30 000000 Nylon 66, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer Lanxess
Trade Name Durethan®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Lanxess Durethan® AKV 30 000000 Nylon 66, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PA 66, 30% glass fibers, injection moldingInformation provided by LANXESS.
Physical Properties Metric English Comments
Specific Gravity 1.36 g/cc
1.36 g/cc
ISO 1183
Bulk Density 0.700 g/cc
0.0253 lb/in³
ISO 60
Moisture Absorption at Equilibrium 2.0 %
2.0 %
50% RH; ISO 62
Water Absorption at Saturation 5.5 %
5.5 %
ISO 62
Linear Mold Shrinkage, Flow 0.00040 cm/cm
0.00040 in/in
Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577
0.0035 cm/cm
0.0035 in/in
150x105x3; 280°C / MT 80°C; 400 bar; ISO 2577
Linear Mold Shrinkage, Transverse 0.00050 cm/cm
0.00050 in/in
Post-shrinkage, 150x105x3; 120°C; 4 hour; ISO 2577
0.0146 cm/cm
0.0146 in/in
150x105x3; 280°C / MT 80°C; 400 bar; ISO 2577
Mechanical Properties Metric English Comments
Ball Indentation Hardness 130 MPa
18900 psi
cond.; ISO 2039-1
230 MPa
33400 psi
d.a.m.; ISO 2039-1
Tensile Strength at Break 125 MPa
18100 psi
cond.; ISO 527-1, -2; 5 mm/min
185 MPa
26800 psi
d.a.m.; ISO 527-1, -2; 5 mm/min
Elongation at Break 3.0 %
3.0 %
d.a.m.; ISO 527-1, -2; 5 mm/min
6.0 %
6.0 %
cond.; ISO 527-1, -2; 5 mm/min
Tensile Modulus 7.00 GPa
1020 ksi
cond.; ISO 527-1, -2; 1 mm/min
10.6 GPa
1540 ksi
d.a.m.; ISO 527-1, -2; 1 mm/min
Flexural Strength 200 MPa

@Strain 6.00 %
 29000 psi

@Strain 6.00 %
 cond., 2 mm/min; ISO 178-A
290 MPa

@Strain 4.00 %
 42100 psi

@Strain 4.00 %
 d.a.m., 2 mm/min; ISO 178-A
Flexural Yield Strength 165 MPa

@Strain 3.50 %
 23900 psi

@Strain 3.50 %
 cond., 2 mm/min; ISO 178-A
Flexural Modulus 5.90 GPa
856 ksi
cond., 2 mm/min; ISO 178-A
8.40 GPa
1220 ksi
d.a.m., 2 mm/min; ISO 178-A
Izod Impact, Notched (ISO) <= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -30.0 °C
 <= 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -40.0 °C
 <= 4.76 ft-lb/in²

@Temperature -40.0 °F
 d.a.m.; ISO 180-1A
<= 10.0 kJ/m²

@Temperature -40.0 °C
 <= 4.76 ft-lb/in²

@Temperature -40.0 °F
 cond.; ISO 180-1A
Charpy Impact Unnotched 7.00 J/cm²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eU
7.00 J/cm²

@Temperature -30.0 °C
 33.3 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eU
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eU
9.00 J/cm²

@Temperature 23.0 °C
 42.8 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eU
Charpy Impact, Notched 1.00 J/cm²

@Temperature 23.0 °C
 4.76 ft-lb/in²

@Temperature 73.4 °F
 d.a.m.; ISO 179-1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 d.a.m.; ISO 179-1eA
1.00 J/cm²

@Temperature -30.0 °C
 4.76 ft-lb/in²

@Temperature -22.0 °F
 cond.; ISO 179-1eA
1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 cond.; ISO 179-1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C

@Temperature 23.0 - 55.0 °C
 13.9 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
CTE, linear, Transverse to Flow 100 µm/m-°C

@Temperature 23.0 - 55.0 °C
 55.6 µin/in-°F

@Temperature 73.4 - 131 °F
 ISO 11359-1, -2
Melting Point 263 °C
505 °F
10°C/min; ISO 11357-1, -3
Deflection Temperature at 0.46 MPa (66 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 1.8 MPa (264 psi) 250 °C
482 °F
ISO 75-1, -2
Deflection Temperature at 8.0 MPa 135 °C
275 °F
ISO 75-1, -2
Vicat Softening Point >= 230 °C

@Load 5.10 kg
 >= 446 °F

@Load 11.2 lb
 120°C/hour; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
 HB

@Thickness 0.126 in
Oxygen Index 23 %
23 %
Method A; ISO 4589-2
Glow Wire Test 600 °C

@Diameter 2.00 mm
 1110 °F

@Diameter 0.0787 in
 GWIT; IEC 60695-2-13
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+12 ohm-cm
1.00e+12 ohm-cm
cond.; IEC 60093
1.00e+15 ohm-cm
1.00e+15 ohm-cm
d.a.m.; IEC 60093
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
cond.; IEC 60093
1.00e+14 ohm
1.00e+14 ohm
d.a.m.; IEC 60093
Dielectric Constant 4.0

@Frequency 100 Hz
 4.0

@Frequency 100 Hz
 d.a.m.; IEC 60250
4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
4.0

@Frequency 1.00e+6 Hz
 4.0

@Frequency 1.00e+6 Hz
 cond.; IEC 60250
10

@Frequency 100 Hz
 10

@Frequency 100 Hz
 cond.; IEC 60250
Dielectric Strength 35.0 kV/mm

@Thickness 1.00 mm
 889 kV/in

@Thickness 0.0394 in
 cond.; IEC 60243-1
40.0 kV/mm

@Thickness 1.00 mm
 1020 kV/in

@Thickness 0.0394 in
 d.a.m.; IEC 60243-1
Dissipation Factor 0.0090

@Frequency 100 Hz
 0.0090

@Frequency 100 Hz
 d.a.m.; IEC 60250
0.018

@Frequency 1.00e+6 Hz
 0.018

@Frequency 1.00e+6 Hz
 d.a.m.; IEC 60250
0.080

@Frequency 1.00e+6 Hz
 0.080

@Frequency 1.00e+6 Hz
 cond.; IEC 60250
0.27

@Frequency 100 Hz
 0.27

@Frequency 100 Hz
 cond.; IEC 60250
Comparative Tracking Index 600 V
600 V
d.a.m.; Solution A; IEC 60112
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
290 °C
554 °F
for test specimens; ISO 294
Mold Temperature 80.0 °C
176 °F
for test specimens; ISO 294
80.0 - 120 °C
176 - 248 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 2 - 6 hour
2 - 6 hour
Moisture Content 0.030 - 0.12 %
0.030 - 0.12 %
residual; Karl Fischer Test
Descriptive Properties Value Comments
ISO Shortname ISO 1874-PA, 66, 14-110, GF30