Lanxess Durethan® AKV 15 H3.0 000000 Nylon 66, 15% Glass Fibers
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Durethan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Durethan® AKV 15 H3.0 000000 Nylon 66, 15% Glass Fibers.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PA 66, 15% glass fibers, injection molding, heat-ageing stabilized
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.239 g/cc | 1.239 g/cc | ISO 1183 |
| Bulk Density | 0.700 g/cc | 0.0253 lb/in³ | ISO 60 |
| Moisture Absorption at Equilibrium | 2.4 % | 2.4 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 7.0 % | 7.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Thickness 2.00 mm |
0.0070 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm |
0.010 in/in @Thickness 0.0787 in |
Mold Temp 80°C; Melt Temp 280°C; 600 bar; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 90.0 MPa | 13100 psi | Conditioned; ISO 2039-1 |
| 190 MPa | 27600 psi | ISO 2039-1 | |
| Tensile Strength at Break | 73.0 MPa | 10600 psi | Conditioned; ISO 527-1,-2 |
| 125 MPa | 18100 psi | ISO 527-1,-2 | |
| Elongation at Break | 2.8 % | 2.8 % | ISO 527-1,-2 |
| 18 % | 18 % | Conditioned; ISO 527-1,-2 | |
| Tensile Modulus | 3.30 GPa | 479 ksi | Conditioned; ISO 527-1,-2 |
| 5.90 GPa | 856 ksi | ISO 527-1,-2 | |
| Flexural Strength | 125 MPa @Strain 7.00 % |
18100 psi @Strain 7.00 % |
Conditioned; ISO 178 |
| 200 MPa @Strain 4.50 % |
29000 psi @Strain 4.50 % |
ISO 178 | |
| Flexural Yield Strength | 90.0 MPa @Strain 3.50 % |
13100 psi @Strain 3.50 % |
Conditioned; ISO 178 |
| 180 MPa @Strain 3.50 % |
26100 psi @Strain 3.50 % |
ISO 178 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | Conditioned; ISO 178 |
| 5.30 GPa | 769 ksi | ISO 178 | |
| Izod Impact, Notched (ISO) | <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A |
| <= 10.0 kJ/m² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A | |
| <= 10.0 kJ/m² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1A | |
| Izod Impact, Unnotched (ISO) | 30.0 kJ/m² @Temperature 23.0 °C |
14.3 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1U |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1U | |
| 30.0 kJ/m² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 180-1U | |
| 75.0 kJ/m² @Temperature 23.0 °C |
35.7 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 180-1U | |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| 3.50 J/cm² @Temperature -30.0 °C |
16.7 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU | |
| 4.00 J/cm² @Temperature -30.0 °C |
19.0 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eU | |
| 5.00 J/cm² @Temperature 23.0 °C |
23.8 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eU | |
| Charpy Impact, Notched | <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eA |
| <= 1.00 J/cm² @Temperature 23.0 °C |
<= 4.76 ft-lb/in² @Temperature 73.4 °F |
Conditioned; ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eA | |
| <= 1.00 J/cm² @Temperature -30.0 °C |
<= 4.76 ft-lb/in² @Temperature -22.0 °F |
Conditioned; ISO 179-1eA | |
| Puncture Energy | 1.50 J @Load <=58.9 kg, Temperature -30.0 °C |
1.11 ft-lb @Load <=130 lb, Temperature -22.0 °F |
ISO 6603-2 |
| 1.70 J @Load <=62.9 kg, Temperature 23.0 °C |
1.25 ft-lb @Load <=139 lb, Temperature 73.4 °F |
ISO 6603-2 | |
| 2.30 J @Load <=140.5 kg, Temperature 23.0 °C |
1.70 ft-lb @Load <=309.8 lb, Temperature 73.4 °F |
Conditioned; ISO 6603-2 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C | 22.2 µin/in-°F | ISO 11359-1,-2 |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C | 50.0 µin/in-°F | ISO 11359-1,-2 |
| Melting Point | 263 °C | 505 °F | ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | >= 250 °C | >= 482 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 230 °C | 446 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 70.0 °C | 158 °F | ISO 75-1,-2 |
| Vicat Softening Point | >= 230 °C | >= 446 °F | 50°C/h; ISO 306 |
| >= 230 °C @Load 5.10 kg |
>= 446 °F @Load 11.2 lb |
120°C/h; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
||
| Glow Wire Test | 650 °C | 1200 °F | IEC 60695-2-12 |
| Shrinkage | 0.10 % @Temperature 120 °C, Time 14400 sec |
0.10 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| 0.20 % @Temperature 120 °C, Time 14400 sec |
0.20 % @Temperature 248 °F, Time 4.00 hour |
Molding Post-shrinkage; ISO 294-4 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+15 ohm | 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz |
3.8 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 4.2 @Frequency 100 Hz |
4.2 @Frequency 100 Hz |
IEC 60250 | |
| Dielectric Strength | 38.0 kV/mm @Thickness 1.00 mm |
965 kV/in @Thickness 0.0394 in |
IEC 60243-1 |
| Dissipation Factor | 0.23 @Frequency 100 Hz |
0.23 @Frequency 100 Hz |
IEC 60250 |
| 0.25 @Frequency 1.00e+6 Hz |
0.25 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | 550 V | 550 V | Solution A, Rating; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | Processing conditions for test specimens; ISO 294 |
| 280 - 300 °C | 536 - 572 °F | Recommended | |
| Mold Temperature | 80.0 °C | 176 °F | Processing conditions for test specimens; ISO 294 |
| 80.0 - 120 °C | 176 - 248 °F | Recommended | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2 - 6 hour | 2 - 6 hour | |
| Moisture Content | 0.030 - 0.12 % | 0.030 - 0.12 % | Residual; Acc. To Karl Fischer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Flammability | Passed US-FMVSS302 | ISO 3795 |
| ISO Shortname | ISO 1874-PA 66,GHR,14-060,GF15 |
Users viewing this material also viewed the following:
- Polykemi AB SCANAMID 66 A12^ QF2515 Nylon 66,Mineral and Glass Fiber Reinforced
- Kingfa LONOY 2100 LT PC/PET Alloy
- SABIC Innovative Plastics LNP LUBRICOMP RCL36S PA 66 (Asia Pacific)
- SABIC Innovative Plastics LNP Thermocomp RW008XXZ PA 66
- Wieland Porta OP M-1 Solder
- Cytec EN-2534 (Conap) Potting and Encapsulation Adhesive
- Cheng Yu Plastic E2325 Flame Retardant PET, 25% Glass Fiber
- SABIC Innovative Plastics LNP VERTON RV00CEXP PA 66 (Europe-Africa-Middle East)
- Styron Magnum™ 4435 ABS
Copyright © lookpolymers.com All Rights Reserved