Dow DOWLEX™ 2027G Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE |
| Manufacturer | Dow Chemical |
| Trade Name | DOWLEX™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow DOWLEX™ 2027G Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
For high speed, thin gauge applications Improved stiffness Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a Information provided by Dow
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.941 g/cc | 0.0340 lb/in³ | ASTM D792 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 4.0 g/10 min | 4.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 16.22 MPa | 2352 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.76 MPa | 1561 psi | ASTM D882 |
| Film Elongation at Break, MD | 575 % | 575 % | ASTM D882 |
| Film Elongation at Break, TD | 740 % | 740 % | ASTM D882 |
| Impact | 1365 | 1365 | [ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882 |
| 1498 | 1498 | [ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 34 g | 34 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 209 g | 209 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 1.34 g/micron | 34.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 8.23 g/micron | 209 g/mil | ASTM D1922 |
| Dart Drop Test | 43.0 g | 0.0948 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.03 MPa | 5661 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 27.98 MPa | 4058 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 127 °C | 261 °F | Dow Method (DSC) |
| Vicat Softening Point | 123 °C | 253 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 4.1 % | 4.1 % | ASTM D1003 |
| Gloss | 86 % | 86 % | 45°; ASTM D2457 |
Users viewing this material also viewed the following:
- Momentive Performance Materials Siloprenâ„¢ CLS 8150 Liquid Silicone Rubber - Self-Bonding / Customized
- Gouda Vuurvast VIBRON 170 M RAPID Dense Vibrating Refractory Castable
- Techmer ES HiFill® PA6/6 CM30 L 30% Mineral Filled
- UBE UBESTA® 3030U Nylon 12 (After Chloroform for 500 hours)
- UBE UBESTA® 3030U Nylon 12 (After Methyl Ethyl Ketone for 1000 hours)
- ExxonMobil Enable™ 35-05HH Metallocene Polyethylene Resin
- Arkema Group Orgalloy® LT 4060ISH Flexible Nylon Alloy (Conditioned)
- Plastcom SLOVAMID 66/6 GF 30 Polyamide 66/6, 30% Glass Fiber (discontinued **)
- Overview of materials for Acrylic, Impact Modified, Molded
- Samsung Cheil Industries Infino® NH-3208GL PC, Glass Filled FR
Copyright © lookpolymers.com All Rights Reserved