LTL Color Compounds ColorFast® NY2115 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | LTL Color Compounds |
| Trade Name | ColorFast® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LTL Color Compounds ColorFast® NY2115 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Super tough nylon 6,6 with excellent chemical resistance and ductilityAll information provided by LTL Color Compounders, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | @ 24 Hours; ASTM D570 |
| Linear Mold Shrinkage | 0.0015 - 0.0020 cm/cm | 0.0015 - 0.0020 in/in | 0.125; ASTM D955 |
| Melt Flow | 30 g/10 min @Load 5.00 kg, Temperature 276 °C |
30 g/10 min @Load 11.0 lb, Temperature 529 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 75 | 75 | ASTM D785 |
| Tensile Strength at Break | 46.9 MPa | 6800 psi | 2.0 in/min; ASTM D638 |
| Tensile Strength, Yield | 52.4 MPa | 7600 psi | 2.0 in/min; ASTM D638 |
| Elongation at Break | 70 % | 70 % | 2.0 in/min; ASTM D638 |
| Elongation at Yield | 18 % | 18 % | 2.0 in/min; ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | 2.0 in/min; ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | 2.0 in/min; ASTM D790 |
| Izod Impact, Notched | 8.54 J/cm @Temperature 22.8 °C |
16.0 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed (0.250"); ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 249 - 282 °C | 480 - 540 °F | |
| Middle Barrel Temperature | 254 - 282 °C | 490 - 540 °F | |
| Front Barrel Temperature | 254 - 282 °C | 490 - 540 °F | |
| Nozzle Temperature | 249 - 277 °C | 480 - 530 °F | |
| Melt Temperature | 268 - 293 °C | 515 - 560 °F | |
| Mold Temperature | 37.8 - 93.3 °C | 100 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | nominal; maximum drying time of 8 hours |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Shot Size | 30 - 60 % | 30 - 60 % | |
| Vent Depth | 0.00381 - 0.00762 cm | 0.00150 - 0.00300 in | |
| Screw Speed | 60 - 120 rpm | 60 - 120 rpm |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3932C TPE, PP Overmold or Standalone use
- SABIC Innovative Plastics Cycoloy® CM6210 PC+ABS (Europe-Africa-Middle East)
- Type P-VSB-32 (Union Carbide) Carbon Fiber
- DuPont Performance Polymers Hytrel® 7246HS BK320 TPC-ET (Unverified Data**)
- Yparex 8207 Polyolefin Adhesive Resin (European Grade) (discontinued **)
- Solvay TECHNYL® A 218 V25 Black 21 N PA66, 25% glass fiber, Conditioned
- Techmer ES HiFill® HIPS TM40 WT 40% Talc Filled
- Wanhua Chemical Wanthane® WHT-1190 Polyester Based TPU
- DuPont Teijin Films Melinex® CORE 2 Polyester Film
- Supreme Petrochem SP 6630 Antistatic Polystyrene
Copyright © lookpolymers.com All Rights Reserved