LG Chemical LUPOY GP5206F PC/ABS+GF20%, Flame Retardance
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Glass Fiber Filled , Polycarbonate (PC) |
| Manufacturer | LG Chemical |
| Trade Name | LUPOY |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOY GP5206F PC/ABS+GF20%, Flame Retardance.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding, PC/ABS+GF20%, Flame Retardance, General PurposeApplication: IT/OA (Housing)CAS: 103598-77-2, 9003-56-9, 68928-70-1, 1309-64-4 and 65997-17-3Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ASTM D792 |
| Maximum Moisture Content | 0.020 | 0.020 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 93.2 MPa @Thickness 3.20 mm |
13500 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 4.0 % @Thickness 3.20 mm |
4.0 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 137 MPa @Thickness 3.20 mm |
19900 psi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Flexural Modulus | 5.69 GPa @Thickness 3.20 mm |
825 ksi @Thickness 0.126 in |
10mm/min; ASTM D790 |
| Izod Impact, Notched | 0.686 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.29 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C @Thickness 6.40 mm |
248 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness >=1.70 mm |
140 °F @Thickness >=0.0669 in |
|
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness >=1.70 mm |
140 °F @Thickness >=0.0669 in |
|
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness >=1.70 mm |
140 °F @Thickness >=0.0669 in |
|
| Flammability, UL94 | V-0 @Thickness >=1.70 mm |
V-0 @Thickness >=0.0669 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 220 - 240 °C | 428 - 464 °F | Injection Molding |
| Middle Barrel Temperature | 235 - 255 °C | 455 - 491 °F | Injection Molding |
| Front Barrel Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Nozzle Temperature | 250 - 265 °C | 482 - 509 °F | Injection Molding |
| Melt Temperature | 235 - 265 °C | 455 - 509 °F | Injection Molding |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Injection Molding |
| Drying Temperature | 75.0 - 85.0 °C | 167 - 185 °F | Injection Molding |
| Dry Time | 3.00 - 5.00 hour | 3.00 - 5.00 hour | Injection Molding |
| Back Pressure | 0.00200 - 0.00600 MPa | 0.290 - 0.870 psi | Injection Molding |
| Screw Speed | 40 - 70 rpm | 40 - 70 rpm | Injection Molding |
Users viewing this material also viewed the following:
- SABIC PP 506P Polypropylene Homopolymer for Raffia Applications
- Park Electrochemical Nelco® N4000-7 FR-4 Epoxy Laminate and Prepreg
- Freudenberg Simrit N445 Nitrile Elastomer (NBR)
- Techmer ES HiFill® PA6/6 GF15 TL5 15% Glass Filled
- Carmel Olefins CARMELCOAT™ MT 34 EC Specialty Polypropylene for Extrusion Coating
- Austin Novel Materials Texalan® 264D Polyester-based TPU
- Arkema Group LOTADER® 3410 Terpolymer Ethylene - Acrylic Ester - Maleic Anhydride
- Ashley Polymers Ashlene® R190H Acetal
Copyright © lookpolymers.com All Rights Reserved