FKuR Kunststoff Fibrolon® F 8530 Biodegradable Wood-Plastic Compound, Fiber Reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Wood and Natural Products |
| Manufacturer | FKuR Kunststoff GmbH |
| Trade Name | Fibrolon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | FKuR Kunststoff Fibrolon® F 8530 Biodegradable Wood-Plastic Compound, Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
FIBROLON® are fiber reinforced compounds. Depending on specific customer requirements either a biodegradable polymer or a polyolefin can be used as the polymeric matrix. With the brand name of FIBROLON® FKuR has developed natural fiber reinforced compounds (Wood-Plastics-Composites: WPC), which, unlike many other WPC, can be injection molded without problems. Furthermore it is possible to process FIBROLON® to complex profiles, panels and hollow profiles and/or into components for the automotive interiors. FIBROLON® compounds are distinguished by high strength and a stiffness comparable to wood.Information Provided by FKuR Kunststoff GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.640 g/cc | 0.0231 lb/in³ | ISO 60 |
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 |
| Melt Flow | 9.0 - 11 g/10 min @Load 5.00 kg, Temperature 190 °C |
9.0 - 11 g/10 min @Load 11.0 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 34.0 MPa | 4930 psi | ISO 527 |
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | ISO 527 |
| Elongation at Break | 3.8 % | 3.8 % | ISO 527 |
| Elongation at Yield | 3.4 % | 3.4 % | ISO 527 |
| Tensile Modulus | 3.80 GPa | 551 ksi | ISO 527 |
| Flexural Modulus | 3.70 GPa | 537 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.17 J/cm² @Temperature 23.0 °C |
5.57 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eU |
| Charpy Impact, Notched | 0.480 J/cm² @Temperature 23.0 °C |
2.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 150 - 160 °C | 302 - 320 °F | ISO 3146-C |
| Vicat Softening Point | 72.0 °C | 162 °F | A; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Melt Volume Flow (cm3/10 min) | 7-9 | ISO 1133; 190°C, 5kg |
Users viewing this material also viewed the following:
- Polimeri Europa Europrene® SOL T 177 Styrene - Butadiene Block Copolymer
- ExxonMobil LD 145.PX Packaging Resin (discontinued **)
- SABIC Innovative Plastics NORYL FXN4020H PPE+HIPS
- Teknor Apex Uniprene® UN-1011A Thermoplastic Elastomer
- Unipetrol Ethylhexanol
- Chengdu Polyster RPM540B Flame Retardant Masterbatch
- Clariant Renol PA2SP0009HW Nylon 6, Heavyweight Compound
- AK Steel ASTM A 607 Class 1 Formable, Grade 55K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- Amity Thermosets ATS 131 Phenolic Molding Organic and graphite Filler, Compression Molded
Copyright © lookpolymers.com All Rights Reserved