- Polymer Property : Melt Flow = 3.0 g/10 min
Polymer Property : Melt Flow = 3.0 g/10 min Product List
Physical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Plastcom SLOVAMID 66 W 30 Polyamide 66, 30% Mineral Filled FeaturesPA 66 with the content of 30% chemically modified mineral filler. Used for grips of electric hand tools, hobby tools, gear wheels, covers of electric tools, flat products, automobile wheel .. |
|||
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| Network Polymers NPS 90-0645 Super High Impact Polystyrene Description: Injection Molding GradeInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 3.0 g/10 min @Load 1.00 kg, Temperature 235 °C |
3.0 g/10 min @Load 2.20 lb, Temperature 455 °F |
Procedure A Condition Q; ASTM D1238 |
| Network Polymers Softflex® 8800 Description: Softflex® Thermoplastic Elastomer AlloyInformation provided by Network Polymers Inc. |
|||
| Melt Flow | 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C |
3.0 - 14 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PC/ABS-G10 General Purpose PC/ABS Alloy, 10% Glass Filled PC/ABS Alloy, General Purpose, 10% Glass FilledProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provi.. |
|||
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D-1238 |
| Chevron Phillips EB6025 HIPS - High Impact Polystyrene
(discontinued **) Rubber modified high impact polystyrene.Applications:Cosmetic packagingShower surroundsPoint of purchase displaysThin-wall injection molding and thermoformingFeatures:Smooth, glossy surface finishGo.. |
|||
| Melt Flow | 3.0 - 14 g/10 min @Load 5.00 kg, Temperature 250 °C |
3.0 - 14 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Polymer Resources PC/ABS-GP1-[color]-EP General Purpose PC/ABS Alloy, Electroplating Grade PC/ABS Alloy, General Purpose, Electroplating GradeProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information p.. |
|||
| Melt Flow | 3.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
3.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| LG Chemical Lupoy NF1005F 03R Polycarbonate Resin Description: LUPOY NF 1005F03R, eco-friendly UL94 V0/1.5 mm, is designed for extrusion products. It combines an excellent physical property balance of heat resistance, transparency and impact streng.. |
|||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | (Condition I) ASTM D-1238-94a |
| Multibase Multi-ABS 802 Utility Grade White Data provided by Multibase. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 400 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Solvay Specialty Polymers KetaSpire® KT-820 NL Polyetheretherketone (PEEK) KetaSpire® KT-820 NL is a low flow grade of unreinforced polyetheretherketone (PEEK) supplied in non-lubricated, natural-color pellet form. KetaSpire® PEEK is produced to the highest industry .. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Specialty Polymers Solef® 32008 Polyvinylidene Fluoride (PVDF) Solef® 32008 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Features: Copolymer; Good Flexibility; Low ViscosityUses: Wire & Cable ApplicationsAdditional .. |
|||
| Melt Flow | 3.0 g/10 min @Load 3.80 kg, Temperature 230 °C |
3.0 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Star Plastics ABS405 Extrusion Grade ABS Information provided by Star Plastics, Inc. |
|||
| Melt Flow | 3.0 g/10 min @Load 10.0 kg, Temperature 200 °C |
3.0 g/10 min @Load 22.0 lb, Temperature 392 °F |
ASTM D1238 |
| Supreme Petrochem SP 6460 High Heat Polystyrene Characteristics High impact and modulus Easy flow High heat resistance & strength Available in any dark colorProcessing Injection moldingApplications Instrument enclosures Automobile interior pa.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Borealis Borcoat™ BB125E Polypropylene Adhesive for Steel Pipe Coating Borcoat BB125E is a chemically modified polypropylene copolymer designed to be used as the tie layer between the epoxy corrosion protection layer and the top-coat polypropylene Borcoat BB108E-1199.B.. |
|||
| Melt Flow | 3.0 g/10 min @Temperature 230 °C |
3.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 3468-01 Polypropylene Homopolymer For High Speed Extrusion DescriptionPolypropylene PP 3468-01 is a specially designed homopolymer for high speed extrusion applications. ApplicationTypical applications of PP 3468-01 include profile extrusions, strapping, r.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Brown 10306 Concentrate Based In Polyethylene DescriptionPOLYBATCH® 10306 is a brown color concentrate based in linear low density polyethylene. This product was formulated to offer color and opacity in polyethylene film applications. POLYBA.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Polyram RamOfin PPH501G4 Polypropylene, 20% Glass Fiber, Flame Retardant Glass fiber 20% reinforced, halogen free, flame retardant polypropylene for injection molding applications.Information provided by Polyram. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| Westlake EP413 Low Density Polyethylene WESTLAKE polyethylene EP413 is a low-density polyethylene recommended for blown or cast film clarity applications. This material has very good optical properties, and is suggested for bakery films ,.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ISO 1133 |
| Total PPH 4026 Polypropylene Homopolymer, Film Polypropylene PPH 4026 is a homopolymer polypropylene with a Melt Flow index of 3 g/10 min for the cast extrusion of films with outstanding stiffness and heat resistance.Polypropylene PPH 4026 is in.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman PAPERMATCH® H-3818 Specialty Masterbatch DescriptionPAPERMATCH® H-3818 is a specialty masterbatch formulated to impart paper-like properties to polyethylene films. PAPERMATCH® H-3818 is a natural color, low opacity grade designed to pro.. |
|||
| Melt Flow | 3.0 g/10 min @Temperature 230 °C |
3.0 g/10 min @Temperature 446 °F |
ASTM D1238 |
| A. Schulman PP 3468-01 Polypropylene Homopolymer For High Speed Extrusion DescriptionPolypropylene PP 3468-01 is a specially designed homopolymer for high speed extrusion applications. ApplicationTypical applications of PP 3468-01 include profile extrusions, strapping, r.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| A. Schulman POLYBATCH™ Silver 70100 Concentrate Based In LDPE DescriptionPOLYBATCH® 70100 is a silver metallic color concentrate based in LDPE. This concentrate was designed to provide opacity and color in polyolefin film and molding applications. POLYBATC.. |
|||
| Melt Flow | 3.0 g/10 min @Load 21.6 kg, Temperature 150 °C |
3.0 g/10 min @Load 47.6 lb, Temperature 302 °F |
ISO 1133 |
| Fainplast Compounds Hax™ HFX 505/2 Crosslinkable HFFR Cable Compound Polyolefin based HFFR silane grafted compound; cross-linkable by heat and moisture and by addition of suitable catalystGrade description:• Sheathing; InsulationInformation provided by Fainplast Com.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 235 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 455 °F |
|
| Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned) Designation ISO 1874-PA12,M,16-120,CF30Rigid grade with carbon fiber filler (30%) for injection molding. Available color: black.Very high rigidity. High strength-to-weight ratio. Very low shrinkage:.. |
|||
| Melt Flow | 3.0 g/10 min | 3.0 g/10 min | ISO 1133 |
| Addiplast Addilene J 220 M20 Polypropylene Copolymer Mineral reinforced, improved rigidityInformation provided by Addiplast. |
|||
| Melt Flow | 3.0 - 7.0 g/10 min | 3.0 - 7.0 g/10 min | |
| Asahi Glass Fluon® P-805UP PFA Perfluoropolymer Fluon® PFA is a copolymer of tetrafluoroethylene (C2F4) and perfluoroalkoxyethylene, which has excellent chemical, electrical, mechanical and surface properties. PFA retains many inherent character.. |
|||
| Melt Flow | 3.0 - 12 g/10 min @Load 5.00 kg, Temperature 200 °C |
3.0 - 12 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Aaron Industries AAROLENE® ARPS MI 100-2 Polystyrene Compounded Resin AAROLENE® ARPS 100 Series Polystyrene Compounded ResinColor may be specified. Melt Flow Index may be specified. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 - 8.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Solvay Specialty Polymers Solef® 31508 Polyvinylidene Fluoride (PVDF)
(Unverified Data**) Solef® 31508 PVDF copolymer is a low viscosity and very flexible grade for Wire & Cable applications.Information provided by Solvay Specialty Polymers. |
|||
| Melt Flow | 3.0 - 8.0 g/10 min @Load 12.5 kg, Temperature 232 °C |
3.0 - 8.0 g/10 min @Load 27.6 lb, Temperature 450 °F |
ASTM D1238 |
| Arkema Group KYNAR FLEX® 2850-00 Polyvinylidene Fluoride Copolymer - Extrusion & Molding Characteristics: Natural resin - translucent, off-white hemispheres. 150°C Temperature rating. High stability in harsh thermal, chemical and ultraviolet environments. High toughness and mechani.. |
|||
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 190 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 374 °F |
ASTM D1238 |
| DuPont Bynel® 41E557 Anhydride-Modified LLDPE Adhesive Resin
(discontinued **) Bynel® Series 4100 resins are anhydride-modified, linear low-density polyethylene (LLDPE) resins. All 4100 Series resins are available in pellet form for use in conventional extrusion and coextrusi.. |
|||