- LG Chemical LUPOL GP-3152F General Purpose Polypropylene, 15% Mineral Fillers, High Impact, Flame Retardant
LG Chemical LUPOL GP-3152F General Purpose Polypropylene, 15% Mineral Fillers, High Impact, Flame Retardant
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Mineral Reinforced |
| Manufacturer | LG Chemical |
| Trade Name | LUPOL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUPOL GP-3152F General Purpose Polypropylene, 15% Mineral Fillers, High Impact, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LUPOL resins, based on polyolefin with a wide range of characteristics, are a family of low cost engineering plastics.Applications: Automotive: Bumper cover, instrument panel, glove box, air cleaner, mud guard, door trim, garnishElectrical and Electronic: Tail lamp housing, air conditioner housing, fan, socket, washing machine partsIndustrial Parts and Household Appliance:Propeller fan, pulley, container, pump container, pump casing, handle and switch cover of electric jar, fan shroud/supportInformation Provided by LG Chem
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Strength | 36.0 MPa | 5220 psi | ASTM D790 |
| Flexural Modulus | 2.35 GPa | 341 ksi | ASTM D790 |
| Izod Impact, Notched | 0.400 J/cm @Temperature 23.0 °C |
0.749 ft-lb/in @Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 130 °C | 266 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 200 - 220 °C | 392 - 428 °F | |
| Middle Barrel Temperature | 200 - 230 °C | 392 - 446 °F | |
| Front Barrel Temperature | 210 - 230 °C | 410 - 446 °F | |
| Nozzle Temperature | 210 - 240 °C | 410 - 464 °F | |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 40.0 - 90.0 °C | 104 - 194 °F | |
| Drying Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Dry Time | 2 - 3 hour | 2 - 3 hour | |
| Injection Pressure | 29.4 - 118 MPa | 4260 - 17100 psi | First |
| 78.45 - 98.07 MPa | 11380 - 14220 psi | Second | |
| Back Pressure | 0.490 - 3.92 MPa | 71.1 - 569 psi | |
| Screw Speed | 40 - 60 rpm | 40 - 60 rpm |
Users viewing this material also viewed the following:
- Osprey Metals 49FeCo2V Cobalt Alloy Powder (Grade 90% - 22)
- Haysite SDL® H400 Polyester Composite
- KB Alloys 5% Strontium Aluminum Alloy
- SABIC Innovative Plastics LNP Thermocomp IF006S PA 6/12 (Asia Pacific)
- A. Schulman POLYBATCH™ 60186U Almond Concentrate Based in LLDPE
- Dow Engage® 8130 Polyolefin Elastomer
- ATI Allvac® VascoMax® C-250 Specialty Steel, Heat Treatment: 927°C (1700°F) + Age
- Axiall 14700 Wire & Cable Flexible PVC
- DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, Mineral Filled Compound (disco
Copyright © lookpolymers.com All Rights Reserved