- Industeel URANUS® 65 310 L Modified Grade - Low C and Si for Nitric Acid Service
Industeel URANUS® 65 310 L Modified Grade - Low C and Si for Nitric Acid Service
| Category | Metal , Ferrous Metal , Austenitic , Stainless Steel , T 300 Series Stainless Steel |
| Manufacturer | Groupe Arcelor |
| Trade Name | URANUS® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Industeel URANUS® 65 310 L Modified Grade - Low C and Si for Nitric Acid Service.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: URANUS® 65 is a 25 Cr 20 Ni austenitic stainless steel with sharp control of the residual elements in order to provide high corrosion resistance properties in boiling 50-65% Nitric acid solutions. The silicon content is kept under 0.3% while the carbon content is lower than 0.015%. Molybdenum additions are also well known to reduce the behavior of the steel in nitric acid solutions. This explains why the molybdenum content is guaranteed lower than 0.3%. The sharp control of Carbon, Silicon and phosphorus contents makes it possible to produce a more stable austenite microstructure, free of intermetallic or carbide precipitations. The alloy is designed for nitric acid applications. The grade is not recommended for concentrated nitric acid purposes or highly oxidizing nitric acid solutions (with Gr VI species...)Information provided by manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.90 g/cc | 0.285 lb/in³ |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Brinell | 155 | 155 | Average |
| Tensile Strength, Ultimate | >= 490 MPa | >= 71100 psi | Minimum Guaranteed |
| Tensile Strength, Yield | >= 215 MPa @Strain 0.200 % |
>= 31200 psi @Strain 0.200 % |
|
| >= 245 MPa @Strain 1.00 % |
>= 35500 psi @Strain 1.00 % |
||
| Elongation at Break | >= 40 % | >= 40 % | |
| Modulus of Elasticity | 195 GPa | 28300 ksi | |
| Poissons Ratio | 0.30 | 0.30 | Calculated |
| Shear Modulus | 75.0 GPa @Temperature 20.0 °C |
10900 ksi @Temperature 68.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 15.8 µm/m-°C @Temperature 0.000 - 100 °C |
8.78 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 16.5 µm/m-°C @Temperature 0.000 - 300 °C |
9.17 µin/in-°F @Temperature 32.0 - 572 °F |
||
| 17.3 µm/m-°C @Temperature 0.000 - 500 °C |
9.61 µin/in-°F @Temperature 32.0 - 932 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Carbon, C | 0.015 % | 0.015 % | |
| Chromium, Cr | 25 % | 25 % | |
| Iron, Fe | 51.635 - 54.485 % | 51.635 - 54.485 % | As remainder |
| Manganese, Mn | <= 2.0 % | <= 2.0 % | |
| Molybdenum, Mo | <= 0.30 % | <= 0.30 % | |
| Nickel, Ni | 20.5 % | 20.5 % | |
| Niobium, Nb (Columbium, Cb) | <= 0.25 % | <= 0.25 % | |
| Silicon, Si | <= 0.30 % | <= 0.30 % |
Users viewing this material also viewed the following:
- Polymax® Maxelast® F7895 TPE, Fire Retardant
- SABIC Innovative Plastics Lexan® 141 PC (Europe-Africa-Middle East)
- Resin Technology Group 408 Oxy-Bond™ Electrically Conductive Epoxy Adhesive
- PolyOne Geon™ 80520 Polyvinyl Chloride, Rigid (PVC, Rigid)
- Industrial Laminates/Norplex NP193M Synthetic Fabric Base Grade
- Guarniflon MFA Fluoropolymer
- SABIC Innovative Plastics PC0703R PC (Asia Pacific)
- SABIC Innovative Plastics LNP THERMOCOMP PH1000A PA 6
- Borealis Daplen™ FS65T20 Polypropylene Compound 20% Mineral Filled, Detergent Resistant
- Chase Plastics CP Pryme® PE200-HD20M General Purpose High Density Polyethylene
Copyright © lookpolymers.com All Rights Reserved