Abatron AboCast/AboCure 8109-4

Category	Polymer , Adhesive , Thermoset , Epoxy
Manufacturer	Abatron
Trade Name	AboCast/AboCure
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Abatron AboCast/AboCure 8109-4.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

Safety hardener (minimum toxicity) version of 8109-3.Processing: 100/10 pbw; Potlife: 2.5 h/20°C (68°F), 30 min/40°C (105°F), 15 min/60°C (140°F); mix at RT; cures in: 24 h/20°C (68°F), 2-3 h/60°C (140°F), 15 min/100°C (212°F).Applications: Laminating, small parts, and potting.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³
Water Absorption	0.60 - 0.70 %	0.60 - 0.70 %	(60x10X4 mm bar) after 10 days at 20°C (77°F)
	1.0 - 1.1 %	1.0 - 1.1 %	(60x10X4 mm bar) after 1 hour at 100°C (212°F)
Viscosity	2000 - 2600 cP	2000 - 2600 cP
Vapor Pressure	<= 0.0000133 bar @Temperature 20.0 °C	<= 0.0100 torr @Temperature 68.0 °F	AboCure
	<= 0.00133 bar @Temperature 100 °C	<= 1.00 torr @Temperature 212 °F	AboCast

Mechanical Properties	Metric	English
Tensile Strength, Ultimate	62.05 MPa	9000 psi
Modulus of Elasticity	3.102 GPa	449.9 ksi
Flexural Yield Strength	89.63 MPa	13000 psi
Compressive Yield Strength	82.74 MPa	12000 psi

Thermal Properties	Metric	English	Comments
CTE, linear	95.0 - 100 µm/m-°C @Temperature 20.0 °C	52.8 - 55.6 µin/in-°F @Temperature 68.0 °F
Maximum Service Temperature, Air	55.0 °C	131 °F	Deflection temperature; load unknown.

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.50e+16 ohm-cm	>= 1.50e+16 ohm-cm
Dielectric Constant	3.6 - 3.9 @Frequency 1e+6 Hz	3.6 - 3.9 @Frequency 1e+6 Hz
	4.0 - 4.1 @Frequency 50 Hz	4.0 - 4.1 @Frequency 50 Hz
Dissipation Factor	0.010 - 0.020	0.010 - 0.020
	0.015 - 0.025 @Frequency 1e+6 Hz	0.015 - 0.025 @Frequency 1e+6 Hz

Processing Properties	Metric	English
Processing Temperature	25.0 °C	77.0 °F
Pot Life	15.0 min @Temperature 60.0 °C	15.0 min @Temperature 140 °F
	30.0 min @Temperature 40.0 °C	30.0 min @Temperature 104 °F
	150 min @Temperature 20.0 °C	150 min @Temperature 68.0 °F