Nilit FRIANYL A63 W-KV30 Nylon 6.6 for injection molding, 30% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL A63 W-KV30 Nylon 6.6 for injection molding, 30% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6 for injection molding, heat stabilized.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 8.0 % | 6.0 - 8.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0050 - 0.015 cm/cm | 0.0050 - 0.015 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 175 MPa | 25400 psi | ISO 2039-1 |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Flexural Strength | 115 MPa | 16700 psi | ISO 178 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ISO 178 |
| Charpy Impact Unnotched | 1.90 J/cm² | 9.04 ft-lb/in² | DIN 53453 |
| NB | NB | ISO 179/1eU | |
| 1.40 J/cm² @Temperature -40.0 °C |
6.66 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| 3.00 J/cm² @Temperature -30.0 °C |
14.3 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² | ISO 179/1eA |
| 0.500 J/cm² | 2.38 ft-lb/in² | DIN 53453 | |
| 0.350 J/cm² @Temperature -30.0 °C |
1.67 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 120 °C | 248 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Eastman Eastalloy DA111 PC+PET Copolyester/Polycarbonate (discontinued **)
- Polimersan Plastics POLITEF® (PTFE)
- Honeywell Capran® Emblem™ 1500M M-Coated Bi-Axially Oriented Nylon Film
- Techmer ES HiFill FR® PBT GF30 FR-S AS 30% Glass Filled
- SABIC Innovative Plastics LNP THERMOCOMP PF005 PA 6 (Europe-Africa-Middle East)
- Styron INSPIREâ„¢ TF1500 ESU Polypropylene
- Chesterton 775 Moisture Shield
- DuPont Performance Polymers Hytrel® G4074 Polyester Elastomer TPC-ET (Unverified Data**)
- Assab Steels 705M Machinery Steel
Copyright © lookpolymers.com All Rights Reserved