LG Chemical LUMID HI1202B(W) PA66, High Impact
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | LG Chemical |
| Trade Name | LUMID |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LG Chemical LUMID HI1202B(W) PA66, High Impact.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Feature: Injection Molding, PA66, High ImpactApplication: Automotive (Covers)CAS No. 32131-17-2 and 9010-79-1Information provided by LG Chemical
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 1.1 % | 1.1 % | ASTM D570 |
| Maximum Moisture Content | 0.10 | 0.10 | Injection Molding |
| Linear Mold Shrinkage, Flow | 0.014 - 0.018 cm/cm @Thickness 3.20 mm |
0.014 - 0.018 in/in @Thickness 0.126 in |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 52.0 MPa @Thickness 3.20 mm |
7540 psi @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Elongation at Break | 60 % @Thickness 3.20 mm |
60 % @Thickness 0.126 in |
50mm/min; ASTM D638 |
| Flexural Yield Strength | 68.6 MPa @Thickness 3.20 mm |
9960 psi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Flexural Modulus | 1.86 GPa @Thickness 3.20 mm |
270 ksi @Thickness 0.126 in |
2.8mm/min; ASTM D790 |
| Izod Impact, Notched | 8.14 J/cm @Thickness 6.40 mm, Temperature 23.0 °C |
15.2 ft-lb/in @Thickness 0.252 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C | 38.9 µin/in-°F | ASTM D696 |
| Melting Point | 260 °C | 500 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C @Thickness 6.40 mm |
149 °F @Thickness 0.252 in |
Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 @Frequency 1.00e+6 Hz |
3.0 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 24.0 kV/mm @Thickness 1.00 mm |
610 kV/in @Thickness 0.0394 in |
ASTM D149 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 275 °C | 500 - 527 °F | Injection Molding |
| Middle Barrel Temperature | 265 - 275 °C | 509 - 527 °F | Injection Molding |
| Front Barrel Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Nozzle Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | Injection Molding |
| Mold Temperature | 60.0 - 90.0 °C | 140 - 194 °F | Injection Molding |
| Drying Temperature | 80.0 - 100 °C | 176 - 212 °F | Injection Molding |
| Dry Time | 4.00 - 5.00 hour | 4.00 - 5.00 hour | Injection Molding |
| Back Pressure | 29.4 - 58.8 MPa | 4260 - 8530 psi | Injection Molding |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm | Injection Molding |
Users viewing this material also viewed the following:
- Polykemi AB POLYfill PPC 05ENH Polypropylene Copolymer, Flame Retardant, Halogen Free
- PEAK Werkstoff DISPAL S260 Aluminum Alloy, AlSi25Cu4Mg, Condition T6
- Karina E 45/56-GEN Gold MBATCH (SP31447) for PVC
- Saint-Gobain Korel® K40-20 Medium Deflection Micro-cellular Polyurethane Foam
- Master Bond Mastersil 153 Two Component, High Temperature Resistance Silicone Adhesive
- A. Schulman PP 3369-01 Polypropylene Medium-Flow Homopolymer Polypropylene
- CP-Polymer-Technik Wellamid® 6000/50 HWUVCP Nylon 6, Impact Modified Until 0°C, UV Stabilized, Heat Stabilized, Dry
- Clariant ABS4500G10BK ABS, 10% Glass Reinforced
- Alliance S-30A Samarium Cobalt Magnetic Material
Copyright © lookpolymers.com All Rights Reserved