Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon P31000A005 0.005" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Liner: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Density	1.06 g/cc	0.0383 lb/in³	Silicone Property; Arlon SQA-TMS-024
Thickness	76.2 microns	3.00 mil	Carrier; Arlon SQA-TMS-003
	127 microns	5.00 mil	Rubber; Arlon SQA-TMS-003

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	35	35	Silicone Property; ASTM D2240
Tensile Strength	6.89 MPa	1000 psi	Silicone Property; ASTM D412
Elongation at Break	650 %	650 %	Silicone Property; ASTM D412

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F

Electrical Properties	Metric	English	Comments
Dielectric Strength	31.5 kV/mm	800 kV/in	Arlon SQA-TMS-020

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Post Cure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	3.00 Month @Temperature 21.1 °C	3.00 Month @Temperature 70.0 °F

Descriptive Properties	Value	Comments
Color	Blue
Total Product Weight (oz/yd2)	5.5	Arlon SQA-TMS-025