Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
Manufacturer | Cossa Polimeri S.r.L. |
Trade Name | ESTAPROP |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Cossa Polimeri ESTAPROP H 0560 HFC Polypropylene, 30% Glass Filled.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D 792 |
Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D 955 |
Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength at Break | 90.0 MPa | 13100 psi | ASTM D 638 |
Elongation at Break | 3.0 % | 3.0 % | ASTM D 638 |
Tensile Modulus | 6.60 GPa | 957 ksi | ASTM D 638 |
Flexural Modulus | 6.00 GPa | 870 ksi | ASTM D 790 |
Izod Impact, Notched | 0.850 J/cm @Temperature -20.0 °C |
1.59 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
1.00 J/cm @Temperature 0.000 °C |
1.87 ft-lb/in @Temperature 32.0 °F |
ASTM D 638 | |
1.10 J/cm @Temperature 23.0 °C |
2.06 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | 120°C/hr; ASTM D 648 |
Vicat Softening Point | 135 °C @Load 5.00 kg |
275 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |