Eurostar Starflam EXCP0132 PA, Mineral Filled, Injection Molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Mineral Filled |
| Manufacturer | Eurostar Engineering Plastics |
| Trade Name | Starflam |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurostar Starflam EXCP0132 PA, Mineral Filled, Injection Molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Starflam EXCP0132 is a Halogen Free and Red Phosphorous Free, Mineral Filled, Polyamide 6 Injection Molding ResinInformation provided by Eurostar.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.40 g/cc | 0.0506 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 70.0 MPa | 10200 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.0 % | 2.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.00 GPa | 870 ksi | 1 mm/min; ISO 527 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² @Temperature -40.0 °C |
0.952 ft-lb/in² @Temperature -40.0 °F |
80x10x4; ISO 180/1A |
| 3.00 kJ/m² @Temperature 23.0 °C |
1.43 ft-lb/in² @Temperature 73.4 °F |
80x10x4; ISO 180/1A | |
| 3.00 kJ/m² @Temperature -20.0 °C |
1.43 ft-lb/in² @Temperature -4.00 °F |
80x10x4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 215 °C | 419 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | Edgew 120x10x4, sp=100 mm; ISO 75/Ae |
| Flammability, UL94 | V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
|
| Glow Wire Test | 850 °C @Thickness 2.50 mm |
1560 °F @Thickness 0.0984 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Zone 1 | 240 - 250 °C | 464 - 482 °F | |
| Zone 2 | 250 - 260 °C | 482 - 500 °F | |
| Zone 3 | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | |
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Moisture Content | 0.20 % | 0.20 % |
Users viewing this material also viewed the following:
- Precision Polymer Engineering V80L Fluoroelastomer Compound
- ExxonMobil Escorene® LD 767.MJ Cast and Compounding Film Resin (discontinued **)
- Michelman® Michem® Lube 190 Anionic polyethylene wax emulsion
- Lubrizol Advanced Materials Pearlstick® D40-70/25 Linear Thermoplastic Polyurethane
- Lucent Polymers 66-01 Nylon 66, General Purpose, Injection Grade
- Lushan PF-300 Adhesive Resin for Multi-layer Barrier Composite Sheet
- Unitika A1025GO PA6, Flame Retardant, Dry
- Aaron Industries AAROLENE® ARPS GP 100-1 Polystyrene Compounded Resin
- ATI Allegheny Ludlum Grade 12 Titanium (UNS R53400)
- Mitsui MILEX™ RX-2325C Low Silicone Rubber Modified Phenolic Resin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved