Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 60% Glass Fiber Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.58 - 1.72 g/cc
0.0571 - 0.0621 lb/in³
Average value: 1.69 g/cc Grade Count:14
Filler Content 60.0 %
60.0 %
Average value: 60.0 % Grade Count:6
Water Absorption 0.350 - 5.00 %
0.350 - 5.00 %
Average value: 2.98 % Grade Count:8
Moisture Absorption at Equilibrium 1.10 - 1.20 %
1.10 - 1.20 %
Average value: 1.18 % Grade Count:5
Linear Mold Shrinkage 0.00100 - 0.00600 cm/cm
0.00100 - 0.00600 in/in
Average value: 0.00257 cm/cm Grade Count:14
Linear Mold Shrinkage, Transverse 0.00200 - 0.00900 cm/cm
0.00200 - 0.00900 in/in
Average value: 0.00544 cm/cm Grade Count:11
Mechanical Properties Metric English Comments
Ball Indentation Hardness 198 - 350 MPa
28700 - 50800 psi
Average value: 281 MPa Grade Count:4
Tensile Strength, Ultimate 155 - 280 MPa
22500 - 40600 psi
Average value: 230 MPa Grade Count:13
150 - 160 MPa

@Temperature 80.0 - 80.0 °C
21800 - 23200 psi

@Temperature 176 - 176 °F
Average value: 155 MPa Grade Count:2
Tensile Strength, Yield 180 - 270 MPa
26100 - 39200 psi
Average value: 230 MPa Grade Count:3
135 - 135 MPa

@Temperature 130 - 175 °C
19600 - 19600 psi

@Temperature 266 - 347 °F
Average value: 135 MPa Grade Count:1
135 - 135 MPa

@Time 1.80e+7 - 7.20e+7 sec
19600 - 19600 psi

@Time 5000 - 20000 hour
Average value: 135 MPa Grade Count:1
Elongation at Break 2.00 - 4.00 %
2.00 - 4.00 %
Average value: 2.53 % Grade Count:16
2.30 - 2.80 %

@Temperature 80.0 - 80.0 °C
2.30 - 2.80 %

@Temperature 176 - 176 °F
Average value: 2.55 % Grade Count:2
Modulus of Elasticity 13.0 - 22.5 GPa
1890 - 3260 ksi
Average value: 18.0 GPa Grade Count:12
10.0 - 13.0 GPa

@Temperature 80.0 - 80.0 °C
1450 - 1890 ksi

@Temperature 176 - 176 °F
Average value: 11.5 GPa Grade Count:2
Flexural Yield Strength 290 - 450 MPa
42100 - 65300 psi
Average value: 389 MPa Grade Count:9
290 - 290 MPa

@Temperature 80.0 - 80.0 °C
42100 - 42100 psi

@Temperature 176 - 176 °F
Average value: 290 MPa Grade Count:2
Flexural Modulus 1.76 - 22.5 GPa
255 - 3260 ksi
Average value: 16.4 GPa Grade Count:9
13.0 - 13.0 GPa

@Temperature 80.0 - 80.0 °C
1890 - 1890 ksi

@Temperature 176 - 176 °F
Average value: 13.0 GPa Grade Count:2
Izod Impact, Notched 1.66 - 1.87 J/cm
3.10 - 3.50 ft-lb/in
Average value: 1.77 J/cm Grade Count:3
Izod Impact, Unnotched (ISO) 76.0 - 80.0 kJ/m²

@Temperature -30.0 - -30.0 °C
36.2 - 38.1 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 78.0 kJ/m² Grade Count:2
Charpy Impact Unnotched 8.60 - 11.5 J/cm²
40.9 - 54.7 ft-lb/in²
Average value: 10.1 J/cm² Grade Count:12
7.60 - 10.5 J/cm²

@Temperature -30.0 - 30.0 °C
36.2 - 50.0 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 8.93 J/cm² Grade Count:8
Charpy Impact, Notched 1.30 - 5.00 J/cm²
6.19 - 23.8 ft-lb/in²
Average value: 3.01 J/cm² Grade Count:12
1.10 - 4.50 J/cm²

@Temperature -30.0 - 30.0 °C
5.24 - 21.4 ft-lb/in²

@Temperature -22.0 - 86.0 °F
Average value: 3.03 J/cm² Grade Count:8
Puncture Energy 31.0 - 31.0 J

@Temperature -30.0 - -30.0 °C
22.9 - 22.9 ft-lb

@Temperature -22.0 - -22.0 °F
Average value: 31.0 J Grade Count:1
Thermal Properties Metric English Comments
CTE, linear 12.6 - 20.0 µm/m-°C
7.00 - 11.1 µin/in-°F
Average value: 17.1 µm/m-°C Grade Count:5
CTE, linear, Transverse to Flow 40.0 - 87.0 µm/m-°C
22.2 - 48.3 µin/in-°F
Average value: 51.8 µm/m-°C Grade Count:4
Melting Point 238 - 265 °C
460 - 509 °F
Average value: 255 °C Grade Count:14
Maximum Service Temperature, Air 100 - 230 °C
212 - 446 °F
Average value: 172 °C Grade Count:5
Deflection Temperature at 0.46 MPa (66 psi) 255 - 257 °C
491 - 495 °F
Average value: 256 °C Grade Count:3
Deflection Temperature at 1.8 MPa (264 psi) 225 - 255 °C
437 - 491 °F
Average value: 239 °C Grade Count:12
Deflection Temperature at 8.0 MPa 195 - 235 °C
383 - 455 °F
Average value: 219 °C Grade Count:9
Flammability, UL94 HB
HB
Grade Count:11
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+10 - 1.00e+15 ohm-cm
1.00e+10 - 1.00e+15 ohm-cm
Average value: 9.50e+13 ohm-cm Grade Count:8
Surface Resistance 1.00e+10 - 8.00e+13 ohm
1.00e+10 - 8.00e+13 ohm
Average value: 1.34e+13 ohm Grade Count:7
Dielectric Strength 18.9 - 40.0 kV/mm
480 - 1020 kV/in
Average value: 25.7 kV/mm Grade Count:5
Comparative Tracking Index 55.0 - 600 V
55.0 - 600 V
Average value: 493 V Grade Count:6
Processing Properties Metric English Comments
Melt Temperature 225 - 320 °C
437 - 608 °F
Average value: 288 °C Grade Count:5
Mold Temperature 71.1 - 100 °C
160 - 212 °F
Average value: 89.1 °C Grade Count:3
Drying Temperature 70.0 - 90.0 °C
158 - 194 °F
Average value: 79.9 °C Grade Count:5
Moisture Content 0.0500 - 0.200 %
0.0500 - 0.200 %
Average value: 0.155 % Grade Count:4
1.10 - 1.10 %

@Temperature 70.0 - 70.0 °C
1.10 - 1.10 %

@Temperature 158 - 158 °F
Average value: 1.10 % Grade Count:4
Injection Pressure 34.5 - 150 MPa
5000 - 21800 psi
Average value: 119 MPa Grade Count:4