Eurostar Staramide BST01 PA6, Impact Modified, Injection Molded

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Eurostar Engineering Plastics
Trade Name Staramide
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Eurostar Staramide BST01 PA6, Impact Modified, Injection Molded.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BST01 is an Impact Modified Polyamide 6 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive supplier.
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.015 - 0.020 cm/cm
0.015 - 0.020 in/in
on Tensile Bar; ISO 294
Mechanical Properties Metric English Comments
Tensile Strength, Yield 70.0 MPa
10200 psi
50 mm/min; ISO 527
Elongation at Break >= 100 %
>= 100 %
50 mm/min; ISO 527
Elongation at Yield 3.8 %
3.8 %
50 mm/min; ISO 527
Tensile Modulus 2.65 GPa
384 ksi
1 mm/min; ISO 527
Izod Impact, Notched (ISO) 7.00 kJ/m²

@Temperature -20.0 °C
 3.33 ft-lb/in²

@Temperature -4.00 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
11.0 kJ/m²

@Temperature 23.0 °C
 5.23 ft-lb/in²

@Temperature 73.4 °F
 Edgew 80x10x4 sp=62; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 91.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
 50.6 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
CTE, linear, Transverse to Flow 115 µm/m-°C

@Temperature 23.0 - 60.0 °C
 63.9 µin/in-°F

@Temperature 73.4 - 140 °F
 ISO 11359-2
Deflection Temperature at 1.8 MPa (264 psi) 75.0 °C
167 °F
Edgew 120x10x4, sp=100 mm; ISO 75/Af
Vicat Softening Point 190 °C
374 °F
B/120; ISO 306
UL RTI, Electrical 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
UL RTI, Mechanical with Impact 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
UL RTI, Mechanical without Impact 65.0 °C

@Thickness 0.750 mm
 149 °F

@Thickness 0.0295 in
65.0 °C

@Thickness 1.50 mm
 149 °F

@Thickness 0.0591 in
65.0 °C

@Thickness 3.00 mm
 149 °F

@Thickness 0.118 in
Flammability, UL94 HB

@Thickness 0.750 mm
 HB

@Thickness 0.0295 in
 IEC 60695-11-10
HB

@Thickness 1.50 mm
 HB

@Thickness 0.0591 in
 IEC 60695-11-10
HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
 IEC 60695-11-10
Electrical Properties Metric English Comments
Comparative Tracking Index 600 V
600 V
IEC 60112
600 V
600 V
M; IEC 60112
Processing Properties Metric English Comments
Rear Barrel Temperature 220 - 230 °C
428 - 446 °F
Zone 1
Middle Barrel Temperature 230 - 240 °C
446 - 464 °F
Zone 2
Front Barrel Temperature 240 - 250 °C
464 - 482 °F
Zone 3
Melt Temperature 240 - 250 °C
464 - 482 °F
Mold Temperature 60.0 - 90.0 °C
140 - 194 °F
Drying Temperature 75.0 - 85.0 °C
167 - 185 °F
Dry Time 4.00 - 6.00 hour
4.00 - 6.00 hour
Moisture Content 0.20 %
0.20 %