LATI Latigray 82-05 CX/90 PA 12

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	LATI
Trade Name	Latigray
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	LATI Latigray 82-05 CX/90 PA 12.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Radiopaque compound based on Polyamide 12 (PA12). Special mineral filler. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.

Physical Properties	Metric	English
Density	4.26 g/cc	0.154 lb/in³
Linear Mold Shrinkage, Flow	0.0070 - 0.0090 cm/cm	0.0070 - 0.0090 in/in
Linear Mold Shrinkage, Transverse	0.0070 - 0.0090 cm/cm	0.0070 - 0.0090 in/in

Mechanical Properties	Metric	English
Tensile Strength at Break	35.0 MPa	5080 psi
Elongation at Break	0.70 %	0.70 %
Tensile Modulus	9.70 GPa	1410 ksi
Charpy Impact Unnotched	1.50 J/cm²	7.14 ft-lb/in²
Charpy Impact, Notched	0.500 J/cm²	2.38 ft-lb/in²

Thermal Properties	Metric	English
Deflection Temperature at 0.46 MPa (66 psi)	160 °C	320 °F
Deflection Temperature at 1.8 MPa (264 psi)	95.0 °C	203 °F
Vicat Softening Point	165 °C @Load 5.00 kg	329 °F @Load 11.0 lb

Electrical Properties	Metric	English	Comments
Volume Resistivity	6500 ohm-cm	6500 ohm-cm
Surface Resistance	5000 ohm	5000 ohm

Processing Properties	Metric	English
Melt Temperature	250 - 270 °C	482 - 518 °F
Mold Temperature	70.0 - 90.0 °C	158 - 194 °F
Drying Temperature	80.0 - 100 °C @Time 10800 sec	176 - 212 °F @Time 3.00 hour

Descriptive Properties	Value	Comments
Electromagnetic reflection	74 dB
ISO Shrinkage - Pressure	60 MPa