- EMS-Grivory Grivory® TSGZ-25/4 PA666-GF25
EMS-Grivory Grivory® TSGZ-25/4 PA666-GF25
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced |
| Manufacturer | EMS-Grivory (EMS-CHEMIE) |
| Trade Name | Grivory® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | EMS-Grivory Grivory® TSGZ-25/4 PA666-GF25.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by EMS Grivory
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.29 g/cc | 0.0466 lb/in³ | ISO 1183 |
| Water Absorption | 6.0 % | 6.0 % | ISO 62 |
| Moisture Absorption | 2.00 % | 2.00 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm | 0.0070 in/in | ISO 294-4, 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 96.0 MPa | 13900 psi | conditioned; ISO 2039-1 |
| 206 MPa | 29900 psi | dry; ISO 2039-1 | |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | conditioned; ISO 527-1/-2 |
| 155 MPa | 22500 psi | dry; ISO 527-1/-2 | |
| Elongation at Break | 3.7 % | 3.7 % | dry; ISO 527-1/-2 |
| 7.4 % | 7.4 % | conditioned; ISO 527-1/-2 | |
| Tensile Modulus | 4.60 GPa | 667 ksi | conditioned; ISO 527-1/-2 |
| 7.90 GPa | 1150 ksi | dry; ISO 527-1/-2 | |
| Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | conditioned; ISO 179/1eU |
| 10.0 J/cm² | 47.6 ft-lb/in² | dry; ISO 179/1eU | |
| 7.30 J/cm² @Temperature 30.0 °C |
34.7 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| Charpy Impact, Notched | 1.40 J/cm² | 6.66 ft-lb/in² | dry; ISO 179/1eA |
| 2.00 J/cm² | 9.52 ft-lb/in² | conditioned; ISO 179/1eA | |
| 0.900 J/cm² @Temperature 30.0 °C |
4.28 ft-lb/in² @Temperature 86.0 °F |
conditioned; ISO 179/1eU | |
| 1.00 J/cm² @Temperature 30.0 °C |
4.76 ft-lb/in² @Temperature 86.0 °F |
dry; ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 20.0 µm/m-°C | 11.1 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1/-3 |
| Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS |
| 180 °C | 356 °F | short term; EMS | |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 85.0 °C | 185 °F | ISO 75-1/-2 |
| Flammability, UL94 | HB | HB | IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | conditioned; IEC 60093 |
| 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | dry; IEC 60093 | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | IEC 60093 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | conditioned; IEC 60243-1 |
| 35.0 kV/mm | 889 kV/in | dry; IEC 60243-1 | |
| Comparative Tracking Index | 600 V | 600 V | dry; IEC 60112 |
| 600 V | 600 V | conditioned; IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Automotive | Interior | |
| Powertrain and Chassis | ||
| Electricals & Electronics | Connectors | |
| Electrical appliances | ||
| Form | Granules | |
| Industry & Consumer goods | Housewares | |
| Mechanical Engineering | ||
| Power transmission | ||
| Sports & Leisure | ||
| Tools & Accessories | ||
| Processing | Injection Molding | |
| Special Characteristics | High impact or impact modified |
Users viewing this material also viewed the following:
- Premix Thermoplastics PREADD AB 172
- SABIC Innovative Plastics Lexan® FXE174R PC (Europe-Africa-Middle East)
- PolyOne Geon™ HTX Ultra LA426 Black 2880 Polyvinyl Chloride Alloy (PVC Alloy)
- ExxonMobil Santoprene® 221-55 Thermoplastic Elastomer (discontinued **)
- H.C. Starck Amperit® 526.077 Agglomerated, Sintered Tungsten Carbide-Cobalt (WC-Co) 83-17
- A. Schulman POLYBATCH™ Grey 8899 Concentrate Based In Polyethylene
- 3M Pronto™ CA-4 Instant Adhesive
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 10 PHR Tricresyl Phosphate
- Hexcel® HexPly® M26/M26T 120°C (250°F) Curing Epoxy Matrix, M26/45%/G1070 Carbon Fabric
Copyright © lookpolymers.com All Rights Reserved