SABIC Innovative Plastics Valox® EH7020HF PBT+PET (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PET + PBT Unreinforced , Polyethylene Terephthalate (PET) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® EH7020HF PBT+PET (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox EH7020HF is a mineral filled PBT/PET that offers good surface appearance, high flow and good heat performance. EH7020HF was developped for automotiove bezel application that require basecoat + top coat metalization. EH7020HF is higher flow version of EH7020.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.420 % | 0.420 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.42 % | 0.42 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0153 - 0.0157 cm/cm | 0.0153 - 0.0157 in/in | on Tensile Bar; SABIC Method |
| 0.0103 - 0.0105 cm/cm @Thickness 3.20 mm |
0.0103 - 0.0105 in/in @Thickness 0.126 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0114 - 0.0118 cm/cm @Thickness 3.20 mm |
0.0114 - 0.0118 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 36 g/10 min @Load 1.20 kg, Temperature 266 °C |
36 g/10 min @Load 2.65 lb, Temperature 511 °F |
ASTM D1238 |
| 64 g/10 min @Load 2.16 kg, Temperature 265 °C |
64 g/10 min @Load 4.76 lb, Temperature 509 °F |
ASTM D1238 | |
| Melt Index of Compound | 52 g/10 min @Load 2.16 kg, Temperature 265 °C |
52 g/10 min @Load 4.76 lb, Temperature 509 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 |
| 57.0 MPa | 8270 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 5 mm/min; ISO 527 |
| 55.0 MPa | 7980 psi | Type I, 5 mm/min; ASTM D638 | |
| 56.0 MPa | 8120 psi | SABIC - Japan Method | |
| Elongation at Break | 1.9 % | 1.9 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| 8.0 % | 8.0 % | SABIC - Japan Method | |
| Elongation at Yield | 1.5 % | 1.5 % | 5 mm/min; ISO 527 |
| 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 4.80 GPa | 696 ksi | 1 mm/min; ISO 527 |
| 5.88 GPa | 853 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 96.0 MPa | 13900 psi | 2 mm/min; ISO 178 | |
| 96.0 MPa | 13900 psi | 6.4 mm; ASTM D790 | |
| Flexural Modulus | 4.68 GPa | 679 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 4.71 GPa | 683 ksi | 2 mm/min; ISO 178 | |
| 4.86 GPa | 705 ksi | 6.4 mm; ASTM D790 | |
| Izod Impact, Notched | 0.310 J/cm | 0.581 ft-lb/in | ASTM D256 |
| 0.310 J/cm @Temperature -30.0 °C |
0.581 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| 2.00 kJ/m² @Temperature -30.0 °C |
0.952 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 4.00 J @Temperature 23.0 °C |
2.95 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 52.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 52.9 µm/m-°C @Temperature -40.0 - 40.0 °C |
29.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 62.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
34.4 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 | |
| Hot Ball Pressure Test | 75.0 °C | 167 °F | IEC 60695-10-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C @Thickness 6.40 mm |
392 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C | 171 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af | |
| 70.0 °C @Thickness 3.20 mm |
158 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 179 °C | 354 °F | Rate B/120; ISO 306 |
| 180 °C | 356 °F | Rate B/50; ASTM D1525 | |
| 180 °C | 356 °F | Rate B/50; ISO 306 |
Users viewing this material also viewed the following:
- Nilit Nilamid A3 H G3 15% Glass Reinforced PA66
- NOVA Chemicals Sclair® FP120-D Octene LLDPE Film Resin
- PolyOne Stat-Tech™ NJ-10SS/000 Nylon 12 - 10% Stainless Steel Reinforced (discontinued **)
- Teknor Apex Monprene® MP-2207B Thermoplastic Elastomer
- Struktol STRUKSILON 8010 Silicone Stabilizer for PU-Rigid Foam
- Covestro Desmopan® 445 Polyurethane
- BASF delta-Valerolactone
- Akzo Nobel Expancel® 051 DE 40 d60 Dry expanded microspheres
- ATI Allegheny Ludlum D2 Tool Steel, UNS T30402
- HP Alloys Alloy C-276, 30% Cold Worked
Copyright © lookpolymers.com All Rights Reserved