- LATI Latamid 66 H2 G/25-V0CT4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
LATI Latamid 66 H2 G/25-V0CT4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | LATI |
| Trade Name | Latamid |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | LATI Latamid 66 H2 G/25-V0CT4 PA 66, 25% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Polyamide 66 (PA66) based compound. Heat stabilized. Glass fibers. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.011 cm/cm | 0.0080 - 0.011 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 75.0 MPa | 10900 psi | |
| Elongation at Break | 2.4 % @Temperature 23.0 °C |
2.4 % @Temperature 73.4 °F |
|
| Tensile Modulus | 9.20 GPa | 1330 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| Charpy Impact, Notched | 0.450 J/cm² | 2.14 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 115 °C | 239 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | |
| Vicat Softening Point | 220 °C @Load 5.00 kg |
428 °F @Load 11.0 lb |
|
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
|
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
||
| Oxygen Index | 34 % | 34 % | |
| Glow Wire Test | 825 °C @Thickness 1.00 mm |
1520 °F @Thickness 0.0394 in |
GWIT |
| 960 °C @Thickness 1.00 mm |
1760 °F @Thickness 0.0394 in |
GWFI/GWT | |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI/GWT | |
| 975 °C @Thickness 2.00 mm |
1790 °F @Thickness 0.0787 in |
GWIT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 70.0 - 100 °C | 158 - 212 °F | |
| Drying Temperature | 90.0 - 100 °C @Time 10800 sec |
194 - 212 °F @Time 3.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage - Pressure | 60 MPa |
Users viewing this material also viewed the following:
- Palm Labs Adhesives Turbo Fuse Series 120 (40 Viscosity) Rapid Bonding Adhesive
- Taiwan Sheen Soon Sheenthane® AS-120H TPU for PU Adhesive
- Polyram Polytron P40B11 Homopolymer Polypropylene, Chemically Coupled 40% LGF
- Abatron AboWeld 48-14/AboCure 48-14 Adhesive/Casting Resin
- Addiplast Addilene H 410 Polypropylene Homopolymer
- Asahi Kasei Thermofil P-40TC-5100 40% Talc Reinforced, Heat Stabilized
- Radici Radilon® S CV300 (cond.) Nylon 6
- Lehmann & Voss LUVOCOM® 1-7233-1 Polyamide 66, with glass fiber, PTFE, lubricant modified, silicone-free
- PolyOne Synprene® RT-3660 Thermoplastic Elastomer - SBC (discontinued **)
Copyright © lookpolymers.com All Rights Reserved