Polymer Property : Tensile Strength at Break = 22500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	155 MPa	22500 psi	STN EN ISO 527-2
Plastcom PLASTAMID® 6 GF 30 005 PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 30% glass fiber, used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, gears, covers..
Tensile Strength at Break	155 MPa	22500 psi	ISO 527
Nilit FRIANYL A63 FK 2010 Nylon 6.6 for injection molding, 20% glass fiber and 10% glass ball reinforced Nylon 6.6 for injection moldingInformation provided by Frisetta Polymer, which merged into Nilit Plastics
Tensile Strength at Break	155 MPa @Temperature 23.0 °C	22500 psi @Temperature 73.4 °F	DAM; 5mm/min; ISO 527
DuPont Performance Polymers Zytel® FE270050 BK099 Nylon 66 (Unverified Data**) Zytel® FE270050 BK099 is a 30% glass reinforced, polyamide 66 resin for gas and water assisted injection molding.Information provided by DuPont
Tensile Strength at Break	155 MPa	22500 psi	10mm/min; ASTM D638
Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech..
Tensile Strength at Break	155 MPa	22500 psi	ISO 527
Grupo Repol DinalonÂ® B1S25 G25 25% Glass Fiber Reinforced Nylon 6 Mechanical properties are for dry as molded samples.Information provided by Grupo Repol.
Tensile Strength at Break	155 MPa	22500 psi	ISO 527-1/-2
Lanxess DurethanÂ® DP AKV 30 HR EF 901510 Nylon 66, 30% Glass Fiber PA 66, injection molding grade, 30% glass fibers, good heat-ageing resistance and hydrolysis resistance, good flowability (Easy Flow)
Tensile Strength at Break	155 MPa	22500 psi	10mm/min; ASTM D638
Kingfa PA6-G30 N101 30% Glass Fiber Reinforced PA6 (general purpose) Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t..
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
Solvay TECHNYLSTARâ„¢ S 60G1 V30 PA6, 30% glass filled, DRY Description: TECHNYLSTARâ„¢ S 60G1 V30 is a reinforced 30% GF organophosphorous flame retarded grade based on a patented high flow polyamide 6 resin (TechnylStar). This product is heat stabilized..
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RFN16 PA 6 LNP* LUBRICOMP* RFN16 is a compound based on Nylon 66 resin containing 30% Glass Fiber, 5% MOS2. Added features of this material include: Wear Resistant.
Tensile Strength at Break	155 MPa	22500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® V9260CS PET (Asia Pacific) Color Stable Glass filled PET
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® V9260CS PET (Europe-Africa-Middle East) Color Stable Glass filled PET
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics ValoxÂ® V9260DCS PET (Europe-Africa-Middle East) Color Stable Glass Filled PET (for Dark colors only)
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF006LXP PA 66 (Asia Pacific) LNP* Thermocomp* RF006LXP is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: Low Extractible.
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP RFP48SXS PA 66 (Europe-Africa-Middle East) LNP* Lubricomp* RFP48SXS is a compound based on Nylon 66 resin containing Glass Fiber, PTFE, Silicone. Added features of this material include: Heat Stabilized.
Tensile Strength at Break	155 MPa	22500 psi	ISO 527-93
Wellman Wellamid® GF30-60 XE-WBK Nylon 6, 30% Glass Reinforced, Weatherable All information provided by Wellman Engineered Resins.
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
Toyobo VYLOPET® EMC341 Injection Molding Polyester Resin, Hydrolysis Resistant Applications: Electric rice cooker partsBathroom appliancesFeatures: Good hydrolysis resistanceInformation provided by Toyobo.
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® 2SV-30H black 9992 PA610-GF30 Product Description: GRILAMID XE 3976 black 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mate..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® EBGM-30 HX PA666-GF30 Product description: Grilon EBGM-30 HX is a specially heat stabilized PA66+PA6 injection molding grade with 30% glass fibers. Grilon EBGM-30 HX has the following important properties: High heat resi..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® LV-50H FWA nat PA12-GF50 Product description: Grilamid LV-50H FWA natural is a 50 % glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following special features: High stiffness combined w..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSGK-30 X PA666-(GF+GB)30 Product description: Grilon TSGK-30 X is a heat stabilized PA66 + PA6 injection molding grade with a 30% reinforcement combination (glass fibers and glass beads). Grilon TSGK-30 X has the following ..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSGZ-25/4 PA666-GF25 Information provided by EMS Grivory
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
Eurostar Starflam RF0077E PA66, 35% Glass Filled, Injection Molded Starflam RF0077E is a Halogen Free and Red Phosphorous Free, Flame Retardant, Glass Fiber Reinforced, Polyamide 66 Injection Molding Resin (also known as RF1007Z270)Information provided by Polymer T..
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOCOMP RF0069XZ PA 66 LNP THERMOCOMP* RF0069XZ is a compound based on Nylon 66 resin containing 30% Glass Fiber. Added features of this material include: Flame Retardant.
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
Beijing Chemical Industry KAIFA® MN201-G35 Nylon 66 Resin 35% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)