Polymer Property : Tensile Strength at Break = 155 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	155 MPa	22500 psi
Plastcom SLOVAMID 6 GF 30 FRG 4 LW PA6, 30% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with nonhalogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°..
Tensile Strength at Break	155 MPa	22500 psi
Plastcom SLOVASTER® B GF 40 PBT reinforced with 40% glass fibre Features: PBT for injection moulding, chemically reinforced with 40% glass fibre. Characterised by excellent properties also at minus temperatures like eg. modulus of elasticity in tension and bendi..
Tensile Strength at Break	155 MPa	22500 psi
Plastcom SLOVAMID 6 NG GF 20 HLS PA6, 20% glass fibre, combined stability FeaturesPA 6 for injection moulding, chemically reinforced with 20% glass fibre, heat stabilized and weather stabilized. Stabilized against hydrolysis. Good surface finisch.Packaging, transport, sto..
Tensile Strength at Break	155 MPa @Temperature 23.0 °C	22500 psi @Temperature 73.4 °F	DAM; 5mm/min; ISO 527
DuPont Performance Polymers Zytel® FE270050 BK099 Nylon 66 (Unverified Data**) Zytel® FE270050 BK099 is a 30% glass reinforced, polyamide 66 resin for gas and water assisted injection molding.Information provided by DuPont
Tensile Strength at Break	155 MPa	22500 psi	5 [mm/min]; ISO 527-1/2
Akro-Plastic Akromid® S3 GF 30 4 (3552) PA 6.10 Dry, 30% Glass Filled (discontinued **) A characteristic property of AKROMID® S (PA 6.10) is that it has a renewable-resource content of up to 70 % and therefore fulfils the current definition of a bioplastic. The plant-based raw materia..
Tensile Strength at Break	155 MPa	22500 psi	10mm/min; ASTM D638
Kingfa PA66-RG301 Flame Retardant, 30% Glass Fiber Reinforced PA66 Features:Flame retardantHigh strengthHigh temperature propertiesGood electric propertiesNo bloomingApplications:Injection moldingConnectorsRelayBobbinsPlugsInformation Provided by Kingfa Sci. & Tech..
Tensile Strength at Break	155 MPa	22500 psi	10mm/min; ASTM D638
Kingfa PA6-G30 N101 30% Glass Fiber Reinforced PA6 (general purpose) Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower t..
Tensile Strength at Break	155 MPa	22500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9300 PEI 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Strength at Break	155 MPa	22500 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics ULTEM AR9300 PEI (Asia Pacific) 30% Glass fiber filled, standard flow Polyetherimide (Tg 217C). Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL GFN1740V PPE+PS (Asia Pacific) Noryl* GFN1740V Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL EXNL1285 PPE+PS (Europe-Africa-Middle East) Noryl* EXNL1285 Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..
Tensile Strength at Break	155 MPa	22500 psi	ISO 527-93
Wellman Wellamid® GF30-60 XE-WBK Nylon 6, 30% Glass Reinforced, Weatherable All information provided by Wellman Engineered Resins.
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
Toyobo VYLOPET® EMC341 Injection Molding Polyester Resin, Hydrolysis Resistant Applications: Electric rice cooker partsBathroom appliancesFeatures: Good hydrolysis resistanceInformation provided by Toyobo.
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® 2SV-30H black 9992 PA610-GF30 Product Description: GRILAMID XE 3976 black 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mate..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® 2SV-30H nat PA610-GF30 Product Description: GRILAMID XE3976 natural 9992 is a 30% glass fiber reinforced, heat stabilized polyamide 610 injection molding grade. This product is to a large extent based on renewable raw mat..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® EBGM-30 HX PA666-GF30 Product description: Grilon EBGM-30 HX is a specially heat stabilized PA66+PA6 injection molding grade with 30% glass fibers. Grilon EBGM-30 HX has the following important properties: High heat resi..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® LV-5H PA12-GF50 Product description: Grilamid LV-5H is a 50% glass fiber reinforced, heat stabilized polyamide 12 injection molding grade with the following product profile: very low water absorptionhigh dimensiona..
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® TSGZ-25/4 PA666-GF25 Information provided by EMS Grivory
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
Eurostar Staramide AG5K PA66, 25% Glass Filled, Injection Molded AG5 is a Heat and Hydrolytically Stabilized, 25% Glass Fiber Reinforced Polyamide 66 Injection Molding ResinInformation provided by Polymer Technology & Services, the North American exclusive suppli..
Tensile Strength at Break	155 MPa	22500 psi	ISO 527-93
Wellman Wellamid® GF33-66/6 XE-WBK 33% Glass Fiber Reinforced, Weatherable Black Nylon 66/6 Description: Glass Fiber Reinforced, Weatherable Black Nylon 66/6Information provided by Wellman.
Tensile Strength at Break	155 MPa	22500 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® XE 4192 black 9992 PA610-GF30 Information provided by EMS Grivory
Tensile Strength at Break	155 MPa	22500 psi	ASTM D638
Beijing Chemical Industry KAIFA® MN201-G35 Nylon 66 Resin 35% glass fiber reinforced, thermal resistantInformation provided by Beijing Chemical Industry Research Institute (Group)
Tensile Strength at Break	155 MPa	22500 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® BG-50 FC PA6-GF50 Product description: Grilon BG-50 FC is a heat stabilized PA6 injection molding grade with 50% glass fibers. Grilon BG-50 FC has the following important properties: Short cycle timesExcellent surfac..
Tensile Strength at Break	155 MPa	22500 psi	5 mm/min; ISO 527
SABIC Innovative Plastics NORYL FE1740PW PPE+PS (Europe-Africa-Middle East) Noryl* FE1740PW Polyphenylene Oxide (PPO) + Polystyrene (PS) resin is a 40 % Glass Reinforced, injection moldable grade with improved hydrolytic stability and with a Tensile Modulus > 11000 MPa; thi..