DuPont Performance Polymers Zytel® FE3071 NC010 Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | DuPont Performance Polymers |
| Trade Name | Zytel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Zytel® FE3071 NC010 Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Zytel® FE3071 NC010 is an intermediate viscosity polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | DAM; ASTM D792 |
| Density | 1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 81.0 MPa @Temperature 23.0 °C |
11700 psi @Temperature 73.4 °F |
DAM; ASTM D638 |
| Tensile Strength, Yield | 82.0 MPa @Temperature 23.0 °C |
11900 psi @Temperature 73.4 °F |
DAM; ISO 527 |
| Elongation at Break | 35 % @Temperature 23.0 °C |
35 % @Temperature 73.4 °F |
DAM; nominal; ISO 527 |
| >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
50mm/min; DAM; ISO 527 | |
| 90 % @Temperature 23.0 °C |
90 % @Temperature 73.4 °F |
DAM; ASTM D638 | |
| Elongation at Yield | 4.0 % @Temperature 23.0 °C |
4.0 % @Temperature 73.4 °F |
DAM; ISO 527 |
| Tensile Modulus | 3.10 GPa @Temperature 23.0 °C |
450 ksi @Temperature 73.4 °F |
DAM; ISO 527 |
| Flexural Modulus | 2.83 GPa @Temperature 23.0 °C |
410 ksi @Temperature 73.4 °F |
DAM; ASTM D790 |
| Izod Impact, Notched | 0.590 J/cm @Temperature 23.0 °C |
1.11 ft-lb/in @Temperature 73.4 °F |
DAM; ASTM D256 |
| Izod Impact, Notched (ISO) | 5.50 kJ/m² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 180/1A |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature 23.0 °C |
2.86 ft-lb/in² @Temperature 73.4 °F |
DAM; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 |
| 262 °C | 504 °F | DAM; ASTM D3418 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | DAM; ASTM D648 |
| 70.0 °C | 158 °F | DAM; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 290 °C | 554 °F | DAM; Optimum |
| 280 - 300 °C | 536 - 572 °F | DAM | |
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum |
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |
| Drying Temperature | 80.0 °C | 176 °F | DAM |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM |
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | DAM |
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM |
| Features | Chemical Resistance, Good | DAM |
| Impact Resistance, Good | DAM | |
| Molecular Wt., Medium | DAM | |
| Forms | Pellets | DAM |
| Generic | Nylon 66 | DAM |
| Material Status | Current | DAM |
| Part Marking Code | >PA66< | ISO 11469; DAM |
| Processing Method | Extrusion | DAM |
| Extrusion | DAM | |
| Injection Molding | DAM | |
| Product Category | Extrusion Resins | DAM |
| Unreinforced Resins | DAM | |
| Resin Identification | PA66 | ISO 1043; DAM |
| RoHS Compliance | Contact Manufacturer | DAM |
| Uses | Filaments | DAM |
| Packaging, Food | DAM |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® JK2000 PC+ABS (Asia Pacific)
- PolyOne Lubri-Tech™ NL-15CF-15GF/5M Nylon 6/12, Carbon/Glass Filled (discontinued **)
- BASF Capron® B85QP Nylon 6 (DAM) (discontinued **)
- Borealis Bormed™ RF830MO Polypropylene Copolymer for Healthcare Applications
- Unitika EX-1020K PA6, Conditioned
- Westlake 1185 PVC
- Tra-Con Tra-Bond FS291 Thixotropic Room Temperature Cure Epoxy Adhesive
- A. Schulman POLYBATCH™ Green 3373 Concentrate Based In Polyethylene
- Elektro-Isola Etronit II Phenolic, Paper Reinforcement, Dark Brown, Sheets
- BASF Luranyl® KR 2454/3 G2 Polyphenylene Ether + Styrene-Butadiene Blend, 10% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved