Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	82.0 MPa	11900 psi	Type I, 51 mm/min; ASTM D638
PolyOne Maxxam™ PPR-30G Black Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Tensile Strength, Yield	82.0 MPa	11900 psi	Type I, 51 mm/min; ASTM D638
PolyOne Maxxam™ PPR-30G Nat Polypropylene Homopolymer (PP Homopolymer) PolyOne's Maxxam™ family of polypropylene- and polyethylene-based products covers a wide range of applications, markets and performance requirements. Standard grades are compounded with calcium car..
Tensile Strength, Yield	82.0 MPa	11900 psi	ASTM D638
Nilit Polynil® P100 Medium Viscosity Nylon 66 Description: Polynil P100 is a grade has a viscosity that has been optimized for monofilament extrusion for high strength monofilaments.Key characteristics: Viscosity number 200 gr/cm3Excellent melt..
Tensile Strength, Yield	82.0 MPa	11900 psi	ASTM D638
Nilit Polynil® P240 High Viscosity Nylon 66 Description: Polynil P240 is a high viscosity NYLON 66 (Viscosity number 290 cm³/gr) that was developed for rod and slab extrusion. It has a high melt stability and a low gel content.Key characteri..
Tensile Strength, Yield	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP FARADEX KX98009 Acetal Copolymer (Europe-Africa-Middle East) LNP* FARADEX* KX98009 is a compound based on Acetal Copolymer resin containing Stainless Steel Fiber, Glass Fiber. Added features include : EMI / RFI Shielding, Electrically Conductive.
Tensile Strength, Yield	82.0 MPa	11900 psi	ASTM D638
NOVA Chemicals Dylark® 250P20 High Performance Glass Filled Styrenic Very high modulus, High heat resistance, Excellent flow characteristics, Excellent adhesion to urethaneApplications: Instrument panel substrates, consoles, Cluster housing, interior trimInjection Sp..
Tensile Strength, Yield	82.0 MPa	11900 psi	SABIC - Japan Method
SABIC Innovative Plastics Lexan® SP7602 PC (Asia Pacific)
Tensile Strength, Yield	82.0 MPa @Temperature 23.0 °C	11900 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66 (Unverified Data**) Zytel® 101F BKB009 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527
Aardvark Polymers AarlonÂ® 2000 Rotational Molding Resin, DAM AarlonÂ® 2000 PA 6/6 is a high performance nylon for rotational molding applications. AarlonÂ® 2000 offers high heat capabilities with exceptional mechanical properties.Information provided by G..
Tensile Strength, Yield	82.0 MPa	11900 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRILOY RX05497 PA 66 (Asia Pacific) LNP LUBRILOY* RX05497 is a compound based on Nylon 66 resin containing Proprietary Lubricant. Added features of this material include: Internally Lubricated.
Tensile Strength, Yield	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON RX06001 PA 66 (Europe-Africa-Middle East) LNP* Stat-kon* RX06001 is a compound based on Nylon 66 resin containing Carbon Fiber. Added features of this material include: Easy Molding, High Impact, Electrically Conductive.
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF003E PC LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing 15% Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527
SABIC Innovative Plastics LNP THERMOCOMP DF003E PC (Asia Pacific) LNP* Thermocomp* DF003E is a compound based on Polycarbonate resin containing Glass Fiber. Added features of this material include: Easy Molding.
Tensile Strength, Yield	82.0 MPa	11900 psi	SABIC - Japan Method
SABIC Innovative Plastics LNP THERMOCOMP Lexan_SP7602 PC (Asia Pacific)
Tensile Strength, Yield	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP THERMOTUF WF006I PBT (Europe-Africa-Middle East) LNP* Thermotuf* WF006I is a compound based on Polybutylene Terephalate resin containing Glass Fiber. Added features of this material include: High Impact.
Tensile Strength, Yield	82.0 MPa	11900 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP STAT-KON AE002 ABS LNP* STAT-KON* AE002 is a compound based on ABS resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive.
Tensile Strength, Yield	82.0 MPa	11900 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-LOY PF303 PA 6 LNP* STAT-LOY* PF303 is a Nylon 6 base resin containing 15% Glass Fiber. Added features of this grade includes: Antistat.
Tensile Strength, Yield	82.0 MPa @Thickness 6.35 mm	11900 psi @Thickness 0.250 in	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+HIPS (Europe-Africa-Middle East) LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Tensile Strength, Yield	82.0 MPa @Thickness 6.35 mm	11900 psi @Thickness 0.250 in	ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP Noryl_FM4025 PPE+PS LNP* Thermocomp* Noryl_FM4025 compound is GR/MR 40%, high modulus structural foam. 10% weight reduction, 0.250"" wall thickness.
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527-1/-2
Unitika A125 PA66, Dry Information provided by Unitika Ltd.
Tensile Strength, Yield	82.0 MPa	11900 psi	ASTM-D638
Polyram PlusTek PA103 Nylon 6.6, Injection Molding Polyamide 6.6 for injection molding applicationsInformation provided by Polyram Ram On Ind.
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527-1/-2
Unitika A1030JR PA6, Dry Information provided by Unitika Ltd.
Tensile Strength, Yield	82.0 MPa @Temperature 23.0 °C	11900 psi @Temperature 73.4 °F	EN ISO 527
Ensinger TECASINT 1611 Polyimide, 30% PTFE Filled (PI) TECASINT is a range of non-melting high temperature polyimides characterized by high strength over a wide range of temperatures, good long term thermal stability, minimal thermal expansion and excel..
Tensile Strength, Yield	82.0 MPa @Temperature 23.0 °C	11900 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® FE3071 NC010 Nylon 66 Zytel® FE3071 NC010 is an intermediate viscosity polyamide 66 resin for injection molding and extrusion.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	82.0 MPa	11900 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® FG101L NC010 Nylon 66 (Unverified Data**) Unreinforced Polyamide 66 with Developed for Food Contact ApplicationsZytel FG101L NC010 is a lubricated polyamide 66 resin for injection molding. It has been developed for consideration into applic..
Tensile Strength, Yield	82.0 MPa	11900 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 101L NC010 Nylon 66 (Unverified Data**) Unreinforced Polyamide 66Zytel 101L NC010 is a lubricated polyamide 66 resin for injection molding.Information provided by DuPont Performance Polymers
Tensile Strength, Yield	82.0 MPa	11900 psi	ISO 527-2
Ascend Performance Materials Vydyne® 21SPC1 Nylon 66, DAM Vydyne® 21SPC1 is a general-purpose, improved-flow, lubricated PA66 resin available in natural color. 21SPC1 offers a balanced combination of properties characterized by high strength, rigidity, go..
Tensile Strength, Yield	82.0 MPa	11900 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® 101F BKB009 Nylon 66 (Unverified Data**) Unreinforced Polyamide 66Zytel 101F BKB009 is an internally lubricated polyamide 66 resin for injection molding. It was developed for fast cycles and high productivity.Information provided by DuPont..