Lanxess Pocan® BF 4130 XF 700051 PBT, 30% Glass Fiber
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled |
| Manufacturer | Lanxess |
| Trade Name | Pocan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lanxess Pocan® BF 4130 XF 700051 PBT, 30% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PBT, 30% glass fibers, injection molding, flame retardant, improved flowability
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.618 g/cc | 0.05845 lb/in³ | ISO 1183 |
| Viscosity Test | 62 cm³/g | 62 cm³/g | Viscosity number; ISO 307, 1157, 1628 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ISO 294-4, 2577 |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 |
| Melt Flow | 28 g/10 min @Load 2.16 kg, Temperature 260 °C |
28 g/10 min @Load 4.76 lb, Temperature 500 °F |
Estimated using room temperature density; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 130 MPa | 18900 psi | ISO 527-1/-2 |
| Elongation at Break | 2.2 % | 2.2 % | ISO 527-1/-2 |
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C | 16.7 µin/in-°F | ISO 11359-1/-2 |
| CTE, linear, Transverse to Flow | 100 µm/m-°C | 55.6 µin/in-°F | ISO 11359-1/-2 |
| Melting Point | 228 °C | 442 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75-1/-2 |
| Deflection Temperature at 8.0 MPa | 147 °C | 297 °F | ISO 75-1/-2 |
| Vicat Softening Point | 205 °C | 401 °F | 50°C/h 50N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 0.750 mm |
V-0 @Thickness 0.0295 in |
IEC 60695-11-10 |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
IEC 60695-11-10 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding; ISO 294 |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding; ISO 10724 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Form | Pellets | |
| ISO Shortname | SO 7792-PBT,GFHR,07-100,GF30; ISO 1043-PBT GF FR(17) | |
| Processing | Injection molding | |
| Region | Asia Pacific | |
| Europe | ||
| Near East/Africa | ||
| North America | ||
| South and Central America |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP THERMOCOMP PFB55 PA 6 (Europe-Africa-Middle East)
- Borealis Borstar® FB1460 HDPE for Film
- Westlake Plastics MediPEEK T Polyetheretherketone for Medical Applications
- Dow AFFINITY™ SE 1400 Polyolefin Plastomer
- Fainplast Compounds GK 85/1 Flexible PVC, Flame Retardant Sheathing Lead Free
- Aclo Accutech Polypropylene Homopolymer HP0334W40L1 Wollastonite Reinforced
- BASF Polystyrol® 158 K Polystyrene (Global)
- Radici Radilon® A RV350 (cond) Nylon 66
- SABIC Innovative Plastics LNP Verton PV007SV_WH8D537 PA 6
- BASF Ultradur B 6550 L PBT
Copyright © lookpolymers.com All Rights Reserved