DSM Stanyl® TS250F8 PA46-GF40 FR

Category	Polymer , Thermoplastic , Nylon , Nylon 46 , Nylon 46, Flame Retarded + Glass Fiber Reinforced
Manufacturer	DSM Engineering Plastics
Trade Name	Stanyl®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DSM Stanyl® TS250F8 PA46-GF40 FR.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

40% Glass Reinforced, Flame Retardant, Heat Stabilized

Physical Properties	Metric	English	Comments
Density	1.77 g/cc	0.0639 lb/in³	dry; ISO 1183
Moisture Absorption	1.25 %	1.25 %	Sim. To ISO 62
Linear Mold Shrinkage, Flow	0.0030 cm/cm	0.0030 in/in	Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse	0.0090 cm/cm	0.0090 in/in	Sim. To ISO 294-4

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	140 MPa	20300 psi	cond; ISO 527-1/-2
	195 MPa	28300 psi	dry; ISO 527-1/-2
	90.0 MPa @Temperature 160 °C	13100 psi @Temperature 320 °F	ISO 527-1/-2
	110 MPa @Temperature 120 °C	16000 psi @Temperature 248 °F	ISO 527-1/-2
Elongation at Break	2.0 %	2.0 %	dry; ISO 527-1/-2
	2.6 %	2.6 %	cond; ISO 527-1/-2
	3.0 % @Temperature 120 °C	3.0 % @Temperature 248 °F	ISO 527-1/-2
	3.0 % @Temperature 160 °C	3.0 % @Temperature 320 °F	ISO 527-1/-2
Tensile Modulus	12.0 GPa	1740 ksi	cond; ISO 527-1/-2
	15.0 GPa	2180 ksi	dry; ISO 527-1/-2
	6.50 GPa @Temperature 160 °C	943 ksi @Temperature 320 °F	ISO 527-1/-2
	9.50 GPa @Temperature 120 °C	1380 ksi @Temperature 248 °F	ISO 527-1/-2
Flexural Modulus	11.0 GPa	1600 ksi	cond; ISO 178
	13.0 GPa	1890 ksi	dry; ISO 178
	5.50 GPa @Temperature 160 °C	798 ksi @Temperature 320 °F	ISO 178
	8.50 GPa @Temperature 120 °C	1230 ksi @Temperature 248 °F	ISO 178
Izod Impact Resistance	1.20 J/cm² @Temperature -40.0 °C	5.71 ft-lb/in² @Temperature -40.0 °F	cond; ISO 180/1A
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	dry; ISO 180/1A
	1.20 J/cm² @Temperature -40.0 °C	5.71 ft-lb/in² @Temperature -40.0 °F	dry; ISO 180/1A
	1.30 J/cm² @Temperature 23.0 °C	6.19 ft-lb/in² @Temperature 73.4 °F	cond; ISO 180/1A
Charpy Impact, Notched	1.10 J/cm² @Temperature 23.0 °C	5.23 ft-lb/in² @Temperature 73.4 °F	dry; ISO 179/1eA
	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	dry; ISO 179/1eA
	1.10 J/cm² @Temperature -30.0 °C	5.23 ft-lb/in² @Temperature -22.0 °F	cond; ISO 179/1eA
	1.20 J/cm² @Temperature 23.0 °C	5.71 ft-lb/in² @Temperature 73.4 °F	cond; ISO 179/1eA

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	25.0 µm/m-°C	13.9 µin/in-°F	dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow	50.0 µm/m-°C	27.8 µin/in-°F	dry; ISO 11359-1/-2
Melting Point	295 °C	563 °F	10°C/min; ISO 11357-1/-3
Maximum Service Temperature, Air	163 °C	325 °F	5000 hours Thermal Index; IEC 60216/ISO 527-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	290 °C	554 °F	dry; ISO 75-1/-2
Flammability, UL94	V-0 @Thickness 1.50 mm	V-0 @Thickness 0.0591 in	dry; IEC 60695-11-10
	V-0 @Thickness 0.750 mm	V-0 @Thickness 0.0295 in	dry; IEC 60695-11-10

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+10 ohm-cm	1.00e+10 ohm-cm	cond; IEC 60093
	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm	dry; IEC 60093
Dielectric Strength	20.0 kV/mm	508 kV/in	cond; IEC 60243-1
	30.0 kV/mm	762 kV/in	dry; IEC 60243-1
Comparative Tracking Index	350 V	350 V	dry; IEC 60112