- SABIC Innovative Plastics LNP THERMOCOMP AW00A ABS (Europe-Africa-Middle East)
SABIC Innovative Plastics LNP THERMOCOMP AW00A ABS (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP AW00A ABS (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* AW00A is a compound based on Acrylonitrile Butadiene Styrene resin containing Wollastonite.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ISO 1183 |
| Water Absorption | 0.24 % @Time 86400 sec |
0.24 % @Time 24.0 hour |
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 5.9 % | 5.9 % | Flexural Strain, break, 2 mm/min; ISO 178 |
| Elongation at Yield | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 3.40 GPa | 493 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 39.0 MPa | 5660 psi | 2 mm/min; ISO 178 |
| Flexural Yield Strength | 49.0 MPa | 7110 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² | 2.38 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 69.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
38.3 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 93.0 µm/m-°C @Temperature 23.0 - 60.0 °C |
51.7 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| Deflection Temperature at 0.46 MPa (66 psi) | 95.0 °C | 203 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 81.0 °C | 178 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Plansee WLZ Lanthanum Oxide and Zirconium Oxide-doped Tungsten
- Shell Carilon® D26VM100 Polyketone, High-Flow Injection Molding Grade (discontinued **)
- LATI Latamid 6 H2 G/55 PA 6, 55% Glass Fiber Reinforced, Heat Stabilized
- Total Polystyrene Impact 8260 Improved Environmental Stress Crack Resistance High Impact Polystyrene
- Hexcel® HexPly® 8552 Epoxy Matrix, Carbon Fabric Form
- A. Schulman POLYFORT™ FPP 3716 Talc Filled Copolymer Polypropylene
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with 0.0 PHR Zinc Stearate
- Dow Corning AMS-C30 Cosmetic Wax
- Devcon Carbide Putty Epoxy
- Carpenter Custom 630 (17-Cr-4Ni) Precipitation Hardening Stainless Steel, Annealed
Copyright © lookpolymers.com All Rights Reserved