POLYMER SEARCH

Cadi 1 MOLD-MOR™

Category	Metal , Nonferrous Metal , Copper Alloy
Manufacturer	Cadi Company
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Cadi 1 MOLD-MOR™.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

A very hard heat treatable copper alloy with moderate electrical conductivity. C18000 offers excellent value for the properties it offers. C18000 is a viable substitute for C17500 and C17510 for many applications.Forms: RodBarPlateShapesInformation provided by Cadi Company.

Physical Properties	Metric	English	Comments
Density	8.80 g/cc	0.318 lb/in³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell B	>= 90	>= 90	Any thickness
Tensile Strength at Break	>= 607 MPa @Thickness >=50.8 mm	>= 88000 psi @Thickness >=2.00 in
	>= 621 MPa @Thickness 25.4 - 50.8 mm	>= 90000 psi @Thickness 1.00 - 2.00 in
	>= 648 MPa @Thickness <=25.4 mm	>= 94000 psi @Thickness <=1.00 in
Tensile Strength, Yield	>= 607 MPa @Strain 0.500 %, Thickness >=50.8 mm	>= 88000 psi @Strain 0.500 %, Thickness >=2.00 in
	>= 621 MPa @Strain 0.500 %, Thickness 25.4 - 50.8 mm	>= 90000 psi @Strain 0.500 %, Thickness 1.00 - 2.00 in
	>= 648 MPa @Strain 0.500 %, Thickness <=25.4 mm	>= 94000 psi @Strain 0.500 %, Thickness <=1.00 in
Modulus of Elasticity	131 GPa	19000 ksi

Thermal Properties	Metric	English
Thermal Conductivity	225 W/m-K	1560 BTU-in/hr-ft²-°F
Melting Point	1068 °C	1955 °F
Liquidus	1068 °C	1955 °F

Component Elements Properties	Metric	English
Chromium, Cr	0.50 %	0.50 %
Copper, Cu	96.5 %	96.5 %
Nickel, Ni	2.4 %	2.4 %
Silicon, Si	0.60 %	0.60 %

Electrical Properties	Metric	English	Comments
Electrical Resistivity	<= 0.00000383 ohm-cm	<= 0.00000383 ohm-cm	Calculated from Min 45 %IACS, up to 3" diameter/any thickness

Processing Properties	Metric	English	Comments
Processing Temperature	649 °C	1200 °F	Brazing, <15 minutes

Descriptive Properties	Value	Comments
RMWA Class	3

Users viewing this material also viewed the following: