Clariant Renol PA611D40 Nylon 612, Glass Fiber Reinforced, Molybdenum Disulfide Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 612 , Nylon 612 with Molybdenum Sulfide Filler |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol PA611D40 Nylon 612, Glass Fiber Reinforced, Molybdenum Disulfide Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.41 g/cc | 1.41 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | ASTM D638 |
| Flexural Yield Strength | 221 MPa | 32000 psi | ASTM D790 |
| Flexural Modulus | 8.27 GPa | 1200 ksi | ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Temperature 22.8 °C |
2.00 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Middle Barrel Temperature | 260 - 288 °C | 500 - 550 °F | |
| Front Barrel Temperature | 266 - 293 °C | 510 - 560 °F | |
| Nozzle Temperature | 266 - 293 °C | 510 - 560 °F | |
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 54.4 - 82.2 °C | 130 - 180 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8623G (UF) Synthetic Oil
- Lubrizol Advanced Materials Pearlstick® 45-90/16 Polycaprolactone based TPU (discontinued **)
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, 10.0 PHR TP-95 Plasticizer
- NOVA Chemicals Novapol® PF-0118-C Butene LLDPE Film Resin
- MarkeTech Cu/Mo/Cu 1:5:1 Laminated Sheet
- Karina E 800-35/1-Y-CRB Ivory PVC Compound
- Iran Petrochemical (PCC) 2004TC37 Low Density Polyethylene
- Latrobe Lescalloy® Jethete M-152 ESR 1.25 RD High Strength Stainless Steel
- Formosa Plastics Formolon® AWS Compound
- 3M Dyneon™ FC 2260 Fluoroelastomer
Copyright © lookpolymers.com All Rights Reserved