Lehmann & Voss LUVOCOM® 19/XCF/20 Polyamide 46, with carbon fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 46 |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 19/XCF/20 Polyamide 46, with carbon fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 270 MPa | 39200 psi | |
| Elongation at Yield | 2.2 % | 2.2 % | |
| 2.9 % | 2.9 % | flexural | |
| Modulus of Elasticity | 19.0 GPa | 2760 ksi | |
| Flexural Strength | 385 MPa | 55800 psi | |
| Flexural Modulus | 16.0 GPa | 2320 ksi | |
| Charpy Impact Unnotched | 7.00 J/cm² | 33.3 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 150 °C | 302 °F | |
| 170 °C | 338 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 290 °C | >= 554 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 100 ohm | <= 100 ohm | |
| Insulation Resistance | <= 100 ohm | <= 100 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 310 °C | 590 °F | mass temp |
| Nozzle Temperature | 280 - 330 °C | 536 - 626 °F | |
| Zone 1 | 285 - 315 °C | 545 - 599 °F | |
| Zone 2 | 305 - 315 °C | 581 - 599 °F | |
| Zone 3 | 305 - 315 °C | 581 - 599 °F | |
| Mold Temperature | 120 - 140 °C | 248 - 284 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 43200 sec |
176 °F @Time 2.00 - 12.0 hour |
Vacuum Dryer |
| 80.0 °C @Time 7200 - 28800 sec |
176 °F @Time 2.00 - 8.00 hour |
Dehumidifying dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | black |
Users viewing this material also viewed the following:
- MV Labs RE450 K2ReCl6 Potassium hexachlororhenate(IV)
- PolyOne Bergamid™ PA66 C20 Black Polyamide 66 (Nylon 66)
- ExxonMobil Escorene® MV-02520 EVA Copolymer, Adhesive and Sealant Grade (discontinued **)
- Multibase Multi-Flex® A 7204 LC TPE Thermoplastic Elastomer
- SABIC Innovative Plastics Valox® 325FC PBT (Europe-Africa-Middle East)
- Techmer ES Luriblend® PA6/6 GF43 ML2 43% Glass Filled
- Samsung Cheil Industries Starex® SD-0150U ABS, Unreinforced
- Silberline Silvex® 410-15-C
- Loctite® 408 Low odor/low bloom Alkoxy Cyanoacrylate Bonding Adhesive
Copyright © lookpolymers.com All Rights Reserved