Clariant Renol 6608-L Nylon 66, High Impact Modified, Lubricated
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Clariant |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Clariant Renol 6608-L Nylon 66, High Impact Modified, Lubricated.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.014 - 0.019 cm/cm | 0.014 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | ASTM D638 |
| Elongation at Yield | 50 % | 50 % | ASTM D638 |
| Flexural Yield Strength | 55.2 MPa | 8000 psi | ASTM D790 |
| Flexural Modulus | 1.59 GPa | 230 ksi | ASTM D790 |
| Izod Impact, Notched | 8.28 J/cm @Temperature 22.8 °C |
15.5 ft-lb/in @Temperature 73.0 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 288 °C | 510 - 550 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Dry Time | 2 - 4 hour @Temperature 79.4 °C |
2 - 4 hour @Temperature 175 °F |
to ensure moisture content is less than 0.2% |
| Injection Pressure | 4.96 - 8.27 MPa | 720 - 1200 psi | Secondary |
| 8.27 - 13.8 MPa | 1200 - 2000 psi | Initial | |
| Back Pressure | 0.345 - 1.72 MPa | 50.0 - 250 psi | |
| Shot Size | 30 - 80 % | 30 - 80 % | |
| Screw Speed | 20 - 100 rpm | 20 - 100 rpm |
Users viewing this material also viewed the following:
- PolyOne Syncure™ S1010B Polyethylene, Crosslinked (XLPE)
- Precision Polymer Engineering H50B Epichlorohydrin
- Polimeri Europa Sinkral® C 442 ABS Resin
- SABIC Innovative Plastics Lexan® FXD141 PC (Europe-Africa-Middle East)
- Shamrock Technologies MicroFLON® 1437 Thermoplastic Grade PTFE Additive
- Solvay RHODASURF® LA 50 Surfactant
- Zircar Zirconia CeW-30 Ceria Woven Textile Insulation
- Loctite® 499 General Purpose Ethyl Cyanoacrylate Bonding Adhesive
- Eurostar Staramide PX08000 PA6, Impact Modified, Injection Molded
- ExxonMobil Escorene® LL-3201 LLDPE/Hexene Premium High Strength 0.6 mil Film, Stiff (discontinued **)
Copyright © lookpolymers.com All Rights Reserved