Polykemi AB SCANBLEND FS7 F20 PBT/ASA Blend, Glass Fiber-Reinforced
| Category | Polymer , Thermoplastic , ASA Polymer , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced |
| Manufacturer | Polykemi AB |
| Trade Name | SCANBLEND |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB SCANBLEND FS7 F20 PBT/ASA Blend, Glass Fiber-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Melt Index of Compound | 17 g/10 min @Load 5.00 kg, Temperature 260 °C |
17 g/10 min @Load 11.0 lb, Temperature 500 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 57.0 MPa | <= 8270 psi | ISO/R527 |
| Elongation at Break | 9.0 % | 9.0 % | ISO/R527 |
| Flexural Strength | <= 98.0 MPa | <= 14200 psi | ISO 178 |
| Flexural Modulus | 5.50 GPa @Temperature 23.0 °C |
798 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -20.0 °C |
2.86 ft-lb/in² @Temperature -4.00 °F |
ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C | 248 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 130 °C @Load 5.001 kg |
266 °F @Load 11.03 lb |
50°C/h; ISO 306 |
| 140 °C @Load 1.00 kg |
284 °F @Load 2.21 lb |
50°C/h; ISO 306 |
Users viewing this material also viewed the following:
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 60 PHR Hi-Sil 243 LD Filler
- Multibase Multi-Flex® D 2010 TPE Thermoplastic Elastomer
- SABIC Innovative Plastics Ultem HFATX200 PEI+PCE
- Wellman Wellamid® MRT1487 BK 32% Mineral Reinforced, Toughened Grade Nylon 66
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 2.5 PHR Sulfur
- Dow Corning SILASTIC® P-1 RTV SILICONE RUBBER & CLEAR CURING AGENT
- ALIMEX ACP 5080R Aluminum Cast Material
- Resinoid 2002-2 Phenolic Molding, Fabric Reinforced
- Overview of materials for Polyethylene Terephthalate (PET), 20% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved