BASF Ultramid® 66 H2 G/35-V0KB NAT 0046 35% Glass Filled PA66 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultramid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultramid® 66 H2 G/35-V0KB NAT 0046 35% Glass Filled PA66 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Ultramid 66 H2 G/35-V0KB NAT0046 is a 35% glass reinforced, heat stabilized injection molding grade. It is a V-0 self-extinguishing grade, with phosphorous. It offers good flowability and mechanical properties. It has excellent electrical properties.Applications: Ultramid 66H2 G/35-V0KB NAT0046 is designed for applications requiring good processing, mechanical integrity and flammability performance.Information provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 175 MPa | 25400 psi | ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| Tensile Modulus | 11.3 GPa | 1640 ksi | ISO 527 |
| Flexural Modulus | 10.7 GPa | 1550 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² @Temperature -40.0 °C |
4.28 ft-lb/in² @Temperature -40.0 °F |
ISO 180 |
| 10.0 kJ/m² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 180 | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -30.0 °C |
4.28 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 247 °C | 477 °F | ISO 75 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 285 - 300 °C | 545 - 572 °F | |
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.050 % | <= 0.050 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | NAT 0046 | |
| Commercial Status | North America |
Users viewing this material also viewed the following:
- Precision Polymer Engineering Perlast® G80S FFKM White Perfluoroelastomer
- PolyOne Maxxam™ DP-9156-5-8000 Polypropylene Copolymer (PP Copolymer)
- SABIC Innovative Plastics Lexan® HFD4472 PC (Asia Pacific)
- Haynes HR-160® alloy, plate, aged 1000 hours at 760°C (1400°F)
- Techmer ES HiFill® PA4/6 CF40 HS 40% Carbon Filled (Dry)
- Master Bond LTX 123 Water-Borne Aliphatic Urethane Adhesive
- Westlake Epolene® C-18P Coating Grade - Branched Medium Molecular Weight Polyethylene Polymer
- Chosun Refractories APC-120 Acid-proof Castable
- Arlon Thermabond® 99A60X008 0.008" (0.203 mm) Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier
Copyright © lookpolymers.com All Rights Reserved