Polymer Property : Tensile Strength at Break = 175 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	<= 175 MPa	<= 25400 psi	ISO/R527
Polykemi AB SCANAMID 66 A13^ F30 Nylon 66, Glass Fiber Reinforced Information provided by Polykemi AB
Tensile Strength at Break	175 MPa	25400 psi	ISO 527
Radici Radilon® A GV H0 30P Nylon 66-GF30 Automotive cooling liquid resistant PA66-GF30 grade designed to resist even in more severe operating condition. Indicated as "top of the class" material.Information provided by Radici group.
Tensile Strength at Break	175 MPa	25400 psi	ASTM D638
LNP Lubricomp® EFL-4036 Polyetherimide, Glass Fiber Reinforcement, PTFE Lubricant (discontinued **) Features: LubricatedForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still ac..
Tensile Strength at Break	175 MPa	25400 psi	ISO 527-1/-2
Lanxess DurethanÂ® DP 2037/30 H2.0 LT 904040 Nylon 6, 30% Glass Fiber PA 6, 30% glass fibers, black colored for laser transmission-welding (laser-transparent), good heat-ageing resistance
Tensile Strength at Break	175 MPa	25400 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP EFL36 PEI (Europe-Africa-Middle East) LNP LUBRICOMP* EFL36 is a compound based on Polyetherimide resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	175 MPa	25400 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electr..
Tensile Strength at Break	175 MPa	25400 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP LUBRICOMP OCP36 PPS LNP* LUBRICOMP* OCP36 is a compound based on Polyphenylene Sulfide resin containing 30% Carbon Fiber, 15% PTFE/Silicone. Added features of this grade include: Wear Resistant, Bearing Grade, Electr..
Tensile Strength at Break	175 MPa	25400 psi	ASTM D638
SABIC Innovative Plastics LNP LUBRICOMP RX06480 PA 66 (Asia Pacific) LNP* LUBRICOMP* RX06480 is a compound based on Nylon 66 resin containing PTFE, Glass Fiber, Silicone. Added features of this material include: Internally Lubricated.
Tensile Strength at Break	175 MPa	25400 psi	5 mm/min; ISO 527
SABIC Innovative Plastics LNP Stat-kon REL36 PA 66 LNP* Stat-Kon* REL36 is a compound based on Nylon 6/6 containing carbon fiber and PTFE. Characteristics of this grade are Statically Conductive.This data was supplied by SABIC-IP for the Americas r..
Tensile Strength at Break	175 MPa	25400 psi	ISO 527
SABIC Innovative Plastics LNP STAT-KON RX05488 PA 66 LNP STAT-KON* RX05488 is a compound based on Nylon 66 resin containing Carbon Fiber, Flame Retardant, Glass Fiber, PTFE. Added features of this material include: Electrically Conductive.
Tensile Strength at Break	175 MPa	25400 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP STAT-KON RX05489 PA 66 LNP* STAT-KON* RX05489 is a compound based on Nylon 66 resin containing 10% Carbon Fiber, 20% Glass Fiber, 15% PTFE/Silicone. Added features of this material include: Electrically Conductive, Wear..
Tensile Strength at Break	175 MPa	25400 psi	ISO 527-93
Wellman Wellamid® GF43-66/6 XE-NBK1 43% Glass Fiber Reinforced, Engineering Grade Nylon 66/6 Description: Glass Fiber Reinforced, Engineering Grade Nylon 66/6Information provided by Wellman.
Tensile Strength at Break	175 MPa	25400 psi	ISO 527-1/-2
DSM Akulon® K224-LG6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break	175 MPa	25400 psi	ISO 527-1/-2
DSM Akulon® Ultraflow™ K-FG6 Nylon 6-30% Glass Reinforced (European Grade) (Dry) The Akulon® product portfolio is engineered for optimum performance to suit different processing techniques and end use markets. Akulon Nylon 6 is used for extrusion applications including barrier ..
Tensile Strength at Break	175 MPa	25400 psi	5 mm/min; ISO 527
CP-Polymer-Technik Wellamid® 6600 CF20 HWCP 20% Carbon Fiber Nylon 66, Heat Stabilized, Dry Information provided by CP-Polymer-Technik GmbH & Co. KG
Tensile Strength at Break	175 MPa	25400 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® XE 4101 black 9225 PA*-GF40 Product description: Grivory XE 4101 is a 40% glass fiber reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamide. This Grivory HT product is partia..
Tensile Strength at Break	175 MPa	25400 psi	conditioned; ISO 527-1/-2
EMS-Grivory Grivory® XE 5106 (GVL-4H V0) PA*-GF40 Product description: Grivory XE 5106 black 9915 is based on a combination of a heat stabilized semi-crystalline Polyamide with a partially aromatic Polyamide. The product is flame retarded and reinf..
Tensile Strength at Break	175 MPa	25400 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN 54G35HSLR BKB336 Polyphthalamide (PPA) 35% Glass Reinforced laser markable PPA High Performance Polyamide Information provided by DuPont Performance Polymers
Tensile Strength at Break	175 MPa	25400 psi	DAM; ISO 527-1/-2
DuPont Performance Polymers Zytel® HTN FR52G45BL BK337 Polyphthalamide (PPA) (Unverified Data**) 45% Glass Reinforced Flame Retardant PPA High Performance Polyamide Zytel HTNFR52G45BL BK337 is a 45% glass reinforced flame retardant lubricated high performance polyamide resin that has been devel..
Tensile Strength at Break	175 MPa @Temperature 23.0 °C	25400 psi @Temperature 73.4 °F	DAM; ISO 527
DuPont Performance Polymers Zytel® PLUS PLS95G40DH1T BK261 Nylon (Unverified Data**) Zytel® PLS95G40DH1T is a 40% GR impact modified PA, made with SHIELD technology, its superior heat & oil resistance combined with the "stone impact resistance" makes it ideal choice for use in seve..
Tensile Strength at Break	175 MPa	25400 psi	dry; ISO 527-1/-2
EMS-Grivory Grivory® BG-50 HM PA6-GF50 Product description: Grilon BG-50 HM is a heat stabilized, normal viscosity, and adhesion modified PA6 injection molding grade with 50% glass fibers. Grilon BG-50 HM has the following important prop..
Tensile Strength at Break	175 MPa	25400 psi	STN EN ISO 527-2
Plastcom SLOVAMID 66/6 GF 30 Polyamide 66/6, 30% Glass Fiber (discontinued **) FeaturesChemically reinforced alloy PA 66 and PA 6 with 30% glass fiber, suitable for mouldings with high strength and toughness also at low temperatures. Used in the automotive, engineering and el..
Tensile Strength at Break	175 MPa	25400 psi	Type I, 5 mm/min; ASTM D638
SABIC Innovative Plastics LNP THERMOCOMP RF007SXN PA 66 LNP* THERMOCOMP* RF007SXN is a Hydro-Stable, 35% Glass Fiber reinforced compound based on Nylon 66. Added features of this grade include: Heat Stabilized, NSF Listed.
Tensile Strength at Break	175 MPa @Temperature 23.0 °C	25400 psi @Temperature 73.4 °F	ISO 527
DuPont Performance Polymers Rynite® 545 BK504 PET (Unverified Data**) Rynite® 545 BK504 is a 45% glass reinforced modified polyethylene terephthalate with good strength and stiffness, excellent dimensional stability and creep resistance.Information provided by DuPont..
Tensile Strength at Break	175 MPa	25400 psi	ISO R 527
Addiplast Addinyl C2 ZV30 Nylon 66/6, 30% Glass Filled Glass fiber reinforced, increased thermal aging stabilityInformation provided by Addiplast.